Method and apparatus for processing thin metal layers

ABSTRACT

A method and apparatus for processing a thin metal layer on a substrate to control the grain size, grain shape, and grain boundary location and orientation in the metal layer by irradiating the metal layer with a first excimer laser pulse having an intensity pattern defined by a mask to have shadow regions and beamlets. Each region of the metal layer overlapped by a beamlet is melted throughout its entire thickness, and each region of the metal layer overlapped by a shadow region remains at least partially unmelted. Each at least partially unmelted region adjoins adjacent melted regions. After irradiation by the first excimer laser pulse, the melted regions of the metal layer are pemitted to resolidify. During resolidification, the at least partially unmelted regions seed growth of grains in adjoining melted regions to produce larger grains. After completion of resolidification of the melted regions following irradiation by the first excimer laser pulse, the metal layer is irradiated by a second excimer laser pulse having a shifted intensity pattern so that the shadow regions overlap regions of the metal layer having fewer and larger grains. Each region of the metal layer overlapped by one of the shifted beamlets is melted throughout its entire thickness, while each region of the metal layer overlapped by one of the shifted shadow regions remains at least partially unmelted. During resolidification of the melted regions after irradiation by the second radiation beam pulse, the larger grains in the at least partially unmelted regions seed growth of even larger grains in adjoining melted regions. The irradiation, resolidification and re-irradiation of the metal layer may be repeated, as needed, until a desired grain structure is obtained in the metal layer.

CLAIM OF PRIORITY

This application claims priority based on the provisional applicationSer. No. 60/239,194 of James S. Im entitled “Process and System forProviding Lateral Solidification of Metallic Films,” filed on Oct. 10,2000.

NOTICE OF GOVERNMENTAL RIGHTS

The invention claimed in the present application was made with fundingfrom the United States Defense Research Project Agency under ContractN66001-98-01-8913. Therefore, the United States Government has certainrights in the invention.

FIELD OF THE INVENTION

The present invention relates to a method and apparatus for processing athin metal layer on a substrate and, more particularly, to a method andapparatus for melting by pulsed irradiation having a predefinedintensity pattern and resolidifying one or more regions of the metallayer so as to control the shape and size of grains, and the locationsand orientation of grain boundaries in the resolidified regions of themetal layer.

BACKGROUND INFORMATION

In the field of semiconductor device processing, there has been a trendto reduce the size of features in integrated circuit devices, includingmetal interconnect lines therein. Due to such decreases in feature size,metal interconnect lines in integrated circuit devices have smallercross-sectional areas and must therefore carry higher current densities.Carrying higher current densities increases the occurrence ofelectromigration in such interconnect lines. Consequently,electromigration is becoming an increasingly common failure mechanism inintegrated circuit devices as the feature sizes in such devices becomesmaller.

Electromigration is observed as a transport of the metal material of ametal interconnect line caused by the transfer of momentum from theelectrons flowing in the interconnect line to the metal ions therein.Electromigration can cause a metal layer interconnect line to fail whenthe transport of metal material creates a void or break in theinterconnect line. Electromigration can also cause dislodged metalmaterial in the metal layer interconnect line to accumulate so as toform bulges sufficiently large to make undesired electrical contact withan adjacent interconnect line. These failures occur most often whenelectron transport takes place parallel to grain boundaries in the metallayer of an interconnect line since grain boundaries can providechannels for the transport of dislodged metal ions.

The problem of failures in metal layer interconnect lines caused byelectromigration may be alleviated by increasing the size of the grainsin the metal layer interconnect lines so as to reduce the total grainboundary density along the direction of electron transport in the metallayer interconnect lines and to control the orientations of grainboundaries so as to form large angles (ideally 90°) with respect to thedirection of electron transport.

In addition to alleviating the problem of electromigration in metallayer interconnect lines in integrated circuit devices, there is ageneral need in other applications for thin metal layers having higherconductance and greater mechanical strength, which may be obtained byincreasing the grain size, and controlling the locations andorientations of grain boundaries in the metal layer. Accordingly, a needclearly exists for a method and apparatus for controlling grain size,grain shape, and the locations and orientations of grain boundaries in ametal layer, including metal layer interconnect lines in integratedcircuit devices.

SUMMARY OF THE INVENTION

In accordance with the present invention, there is provided a method forprocessing a metal layer disposed on the substrate comprising the stepsof irradiating the metal layer with a first radiation beam pulse (e.g.,an excimer laser beam pulse) having an intensity pattern that includesat least one “shadow region” having no radiation intensity, and at leastone “beamlet” having full radiation intensity of the beam. The intensityof the beamlet is such that each region of the metal layer that isoverlapped by a beamlet is melted throughout its entire thickness, andeach region of the metal layer that is overlapped by a shadow regionremains at least partially unmelted. Each melted region adjoins at leastone adjacent at least partially unmelted region.

After irradiation by the first radiation beam pulse, each melted regionof the metal layer is permitted to cool and resolidify. Duringresolidification of each melted region, grains grow therein from eachadjoining at least partially unmelted region until such growing grainsabut (i.e., impinge on) other grains growing in the same melted regionafter the abutting grains have grown by a characteristic growthdistance. Thereafter, the first radiation beam pulse becomes a previousradiation beam pulsed for further processing, and the metal layer isirradiated by a further radiation beam pulse having the same intensitypattern as the previous radiation beam pulse, but where the at least onebeamlet and the at least one shadow region thereof have shifted withrespect to the metal layer by a distance less than the characteristicgrowth distance of the grains growing during resolidification afterirradiation by the previous radiation beam pulse. When the metal layeris irradiated by the further radiation beam pulse, each region of themetal layer overlapped by a shifted beamlet is melted throughout itsentire thickness, and each region of the metal layer overlapped by ashifted shadow region remains at least partially unmelted. Each meltedregion adjoins at least one adjacent at least partially unmelted region.

After irradiation by the further radiation beam pulse, each meltedregion of the metal layer is permitted to cool and resolidify. Duringresolidification of each melted region, grains grow therein from eachadjoining at least partially unmelted region until such growing grainsabut other grains growing in the same melted region after the abuttinggrains have grown by an abutting grain growth distance. Thereafter, thefurther radiation beam pulse becomes the previous radiation pulse forfurther processing, and the steps of (1) irradiation of the metal layerwith a further radiation beam pulse having the same intensity pattern asthe previous radiation beam pulse but where the at least one beamlet andthe at least one shadow region are further shifted with respect to themetal layer by less than the characteristic growth distance, and (2)resolidification of each melted region of the metal layer afterirradiation by the further radiation beam pulse are repeated, if needed,until a desired grain structure is obtained in the metal layer.

The radiation beam pulse may be a laser beam pulse, an electron beampulse, an ion beam pulse or other radiation beam pulse. The intensitypatterns of the radiation beam pulses are defined by a mask throughwhich the radiation beam pulses pass, and the shifting of the intensitypattern with respect to the metal layer may be accomplished by eithershifting the substrate having the metal layer or shifting the mask.

In accordance with a first exemplary embodiment of the method of thepresent invention, the metal layer is prepatterned into one or moremetal layer strips each having a respective predefined contour, and theintensity pattern of the first radiation beam pulse has one or moreseries of multiple, regularly spaced, relatively small, dot-like shadowregions, each series of shadow regions overlapping respective regionsalong the center line of a respective one of the one or more metal layerstrips. The intensity pattern of the first radiation beam pulse alsoincludes a beamlet that overlaps all regions of the one or more metallayer strips not overlapped by the shadow regions. After severaliterations of irradiation of the one or more metal layer strips withradiation beam pulses, where the intensity pattern of each pulse is thesame but shifted with respect to that of a previous pulse, andresolidification of each melted region after each irradiation, a desiredgrain structure is obtained in which each one of the one or more metallayer strips has single-grain regions separated by respective grainboundaries that are each approximately perpendicular to the metal stripat the location of the grain boundary.

According to a second exemplary embodiment of the method of the presentinvention, the metal layer is prepatterned into one or more metal layerstrips each having a respective predefined contour. The intensitypattern of the first radiation beam pulse has one or more relativelynarrow strip-like shadow regions each overlapping the center line of arespective one of the metal layer strips, and a beamlet that overlapsall regions of the one or more metal layer strips not overlapped by theshadow regions. After several iterations of irradiation of the one ormore metal layer strips by radiation beam pulses, each having the sameintensity pattern as that of the first pulse but shifted with respect tothat of a previous pulse, and resolidification of each melted regionafter each irradiation, the grain structure of each metal layer stripcomprises relatively large grains with grain boundaries that form largeangles with respect to the metal layer strip at respective locations ofthe grain boundaries.

According to a third exemplary embodiment of the method of the presentinvention, a metal layer is irradiated by a first radiation beam pulsehaving an intensity pattern that includes an array of multiple,relatively small, dot-like shadow regions disposed at respectiveintersections of regularly spaced, mutually perpendicular diagonallines, and a beamlet that overlaps all regions of the metal layer notoverlapped by the shadow regions. Each region of the metal layeroverlapped by the beamlet is melted throughout its entire thickness,while each region of metal layer overlapped by one of the shadow regionsremains at least partially unmelted. Each melted region adjoinsrespective adjacent melted regions. After irradiation by the firstradiation beam pulse, each melted region is permitted to cool andresolidify. During resolidification of each melted region, grains growfrom each at least partially unmelted region in each adjoining meltedregion. The spacings of the at least partially unmelted regions, asdetermined by the spacings of the shadow regions, are such that grainsgrowing from each at least partially unmelted region abut grains growingfrom neighboring at least partially unmelted regions after the abuttinggrains have grown by an abutting grain growth distance. After severaliterations of irradiation by radiation beam pulses each having the sameintensity pattern but shifted with respect to that of a previous pulse,and resolidification of each melted region after each radiation beampulse, the grain structure of the metal layer comprises generally squaresingle-grain regions with diagonal grain boundaries.

In accordance with the fourth exemplary embodiment of the method of thepresent invention, the intensity pattern of each radiation beam pulseincludes regularly spaced beamlets in the shape of repeating chevronswhere adjacent repeating chevron-shaped beamlets are staggered withrespect to one another such that the peaks of each repeatingchevron-shaped beamlet are aligned with respective troughs of adjacentrepeating chevron-shaped beamlets, and the troughs of each repeatingchevron-shaped beamlet are aligned with respective peaks of adjacentrepeating chevron-shaped beamlets. The intensity pattern of eachradiation beam pulse also includes shadow regions each positioned inbetween and adjoining respective adjacent beamlets. When a metal layeris irradiated by a radiation beam pulse having such an intensitypattern, each region overlapped by a respective one of the beamlets ismelted throughout its entire thickness, and each region overlapped by arespective one of the shadow regions remains at least partiallyunmelted. Each one of the melted regions has the shape of a repeatingchevron with opposing at least partially unmelted edges. Afterirradiation by the radiation beam pulse, each one of the melted regionscools and resolidifies. During resolidification of each melted region,grains grow from each of the opposing edges of the melted region inopposite directions towards one another in the melted region until thegrains growing from the opposing edges abut one another alongapproximately the center line of the repeating chevron-shaped meltedregion after the abutting grains have grown by a characteristic growthdistance. The beamlets and shadow regions of the intensity pattern of afurther radiation beam pulse are shifted with respect to the metal layerin the direction of the peaks of the repeating-chevron-shaped beamletsby a distance less than the characteristic growth distance. The grainstructure obtained after multiple iterations of irradiation andresolidification has adjoining single grain regions each having agenerally hexagonal shape.

According to a fifth exemplary embodiment of the method of the presentinvention, the intensity pattern of the first radiation beam pulse has aplurality of regularly spaced, relatively narrow, linear, stripe-likeshadow regions, and a plurality of regularly spaced, relatively wide,linear, stripe-like beamlets, each one of the beamlets being positionedin between and adjoining respective adjacent shadow regions. When ametal layer is irradiated by the first radiation beam pulse, each regionof the metal layer overlapped by a respective one of the beamlets ismelted throughout its entire thickness, and each region of the metallayer overlapped by a respective one of the shadow regions remains atleast partially unmelted. Each at least partially unmelted regionadjoins respective adjacent melted regions. After irradiation by thefirst radiation beam pulse, each melted region of the metal layer ispermitted to resolidify. During resolidification of each melted region,respective grains grow therein from adjoining at least partiallyunmelted regions in opposite directions towards one another, and abutone another along a respective one of a plurality of first grainabutment boundaries after the abutting grains have grown by a firstabutting grain growth distance. After completion of resolidificationfollowing irradiation by the first radiation beam pulse, the metal layeris irradiated by a second radiation beam pulse having the same intensitypattern as the first radiation beam pulse, but where the shadow regionsand beamlets thereof are shifted in a direction perpendicular to thefirst grain abutment boundaries by a distance at least equal to thewidth of the shadow regions but less than the first abutting graingrowth distance. When the metal layer is irradiated by the secondradiation beam pulse, each region of the metal layer overlapped by arespective one of the shifted beamlets is melted throughout its entirethickness, and each region of the metal layer overlapped by a respectiveone of the shifted shadow regions remains at least partially unmelted.Each at least partially unmelted region adjoins respective adjacentmelted regions. After irradiation by the second radiation beam pulse,the melted regions of the metal layer are permitted to cool andresolidify. During resolidification of each melted region, respectivesingle grains grow therein from adjoining at least partially unmeltedregions in opposite directions towards one another, and abut one anotheralong a respective one of a plurality of second grain abutmentboundaries after the abutting single grains have grown by the firstabutting grain growth distance. Upon completion of resolidification ofthe melted regions after irradiation by the second radiation beam pulse,the metal layer has a grain structure comprising relatively long singlegrains extending between respective adjacent second grain abutmentboundaries and having lateral grain boundaries approximatelyperpendicular to the second grain abutment boundaries.

According to a sixth exemplary embodiment of the method of the presentinvention, after completion of resolidification of the melted regions ofthe metal layer following irradiation by the second radiation beam pulsein the fifth exemplary embodiment described above, the metal layer onthe substrate is rotated by 90° with respect to the second grainabutment boundaries. The rotated metal layer is then irradiated with athird radiation beam pulse having an intensity pattern that includes aplurality of regularly spaced, relatively narrow, linear, stripe-likeshadow regions, each one being perpendicular to the second grainabutment boundaries of the grain structure of the rotated metal layer,and a plurality of regularly spaced, relatively wide, linear stripe-likebeamlets also perpendicular to the second grain abutment boundaries.Each one of the beamlets is positioned in between and adjoiningrespective adjacent shadow regions. When each point on the rotated metallayer is irradiated by the third radiation beam pulse, each region ofthe metal layer overlapped by a respective one of the beamlets is meltedthroughout its entire thickness, and each region of the metal layeroverlapped by a respective one of the shadow regions remains at leastpartially unmelted. Each at least partially unmelted region adjoinsrespective adjacent melted regions. After irradiation by the thirdradiation beam pulse, each melted region of the metal layer is permittedto cool and resolidify. During resolidification of each melted region,different single grains grow from each at least partially unmeltedregion into each adjoining melted region, and in each melted regionrespective grains grow from adjoining at least partially unmeltedregions in opposite directions towards one another, and abut one anotheralong a respective one of a plurality of second grain abutmentboundaries after the abutting single grains have grown by a secondabutting grain growth distance. The abutting single grains each have adimension along the third grain abutment boundaries equal to thedistance between adjacent second grain abutment boundaries. Aftercompletion of resolidification of the melted regions of the metal layerafter irradiation by the third radiation beam pulse, each point on themetal layer is irradiated by a fourth radiation beam pulse having thesame intensity pattern as the third radiation beam pulse, but where theshadow regions and beamlets thereof are shifted in a directionperpendicular to the third grain abutment boundaries by a distance atleast equal to the width of the shadow regions but less than the secondabutting grain growth distance. When each point on the metal layer isirradiated by the fourth radiation beam pulse, each region of the metallayer overlapped by a respective one of the shifted beamlets is meltedthroughout its entire thickness, and each region of the metal layeroverlapped by a respective one of the shifted shadow regions remains atleast partially unmelted. Each at least partially unmelted regionadjoins respective adjacent melted regions. After irradiation by thefourth radiation beam pulse, each melted region of the metal layer ispermitted to cool and resolidify. During resolidification of each meltedregion, respective single grains grow from each at least partiallyunmelted region into each adjoining melted region, and in each meltedregion respective single grains grow from adjoining at least partiallyunmelted regions in opposite directions towards one another, and abutone another along a respective one of a plurality of fourth grainabutment boundaries after the abutting single grains have grown by thesecond abutting grain growth distance. Upon completion ofresolidification of the melted regions after irradiation by the fourthradiation beam pulse, the metal layer has a grain structure comprisingan array of generally rectangular-shaped single-grain regions inrespective rows and columns, each rectangular-shaped single-grain regionhaving a dimension on two opposite sides equal to the distance betweenadjacent second grain abutment boundaries and having a dimension on theother two opposite sides equal to the distance between adjacent fourthgrain abutment boundaries.

According to a seventh exemplary embodiment of the method of the presentinvention, the metal layer is in the form of a relatively narrow metallayer strip having a predefined contour. The width of the relativelynarrow metal layer strip is sufficiently small so as to allow onlysingle grains to grow therein. The metal layer strip is irradiated by afirst radiation beam pulse having an intensity pattern that includes aplurality of relatively narrow, linear, stripe-like shadow regionspositioned at regular intervals along the metal layer strip and abeamlet overlapping all regions of the metal layer strip not overlappedby a respective one of the shadow regions. Each region of the metallayer strip overlapped by the beamlet is melted throughout its entirethickness, and each region of the metal layer strip overlapped by arespective one of the shadow regions remains at least partiallyunmelted. Each at least partially unmelted region adjoins respectiveadjacent melted regions. After irradiation by the first radiation beampulse, each melted region of the metal layer strip is permitted to cooland resolidify. During resolidification of each melted region, differentsingle grains grow from each at least partially unmelted region in eachadjoining melted region, and in each melted region respective singlegrains grow from adjoining at least partially unmelted regions inopposite directions towards one another, and abut one another at arespective one of a plurality of first grain abutment boundaries afterthe abutting single grains have grown by an abutting grain growthdistance. After completion of resolidification of each melted regionfollowing irradiation by the first radiation beam pulse, the metal layerstrip is irradiated with a second radiation beam pulse having the sameintensity pattern as the first radiation beam pulse, but where each oneof the shadow regions is shifted along the metal layer strip by adistance greater than the width of the shadow regions but less than theabutting grain growth distance. The beamlet of the intensity pattern ofthe second radiation beam pulse is also shifted with respect to themetal layer but still overlaps all regions of the metal layer strip notoverlapped by the shadow regions. When the metal layer strip isirradiated by the second radiation beam pulse, each region of the metallayer strip overlapped by the shifted beamlet is melted throughout itsentire thickness, and each region of the metal layer strip overlapped bya respective one of the shifted shadow regions remains at leastpartially unmelted. Each at least partially unmelted region adjoinsrespective adjacent melted regions. After irradiation by the secondradiation beam pulse each melted region of the metal layer strip ispermitted to cool and resolidify. During resolidification of each meltedregion, a respective single grain grows from each at least partiallyunmelted region in each adjoining melted region, and in each meltedregion respective single grains grow from adjoining at least partiallyunmelted regions in opposite directions towards one another, and abutone another at a respective one of a plurality of second grain abutmentboundaries after the abutting single grains have grown by the abuttinggrain growth distance. After completion of resolidification of eachmelted region following the irradiation by the second radiation beampulse, the metal layer strip has a grain structure comprising regions ofsingle grains extending between respective adjacent ones of the secondgrain abutment boundaries. Each second grain abutment boundary issubstantially perpendicular to the metal layer strip at the location ofeach second grain abutment boundary.

According to an eighth exemplary embodiment of the method of the presentinvention, the metal layer comprises at least one relatively narrowmetal layer strip having at least one segment and a respectivepredefined contour having a Manhattan geometry. The width of each one ofthe at least one relatively narrow metal layer strip is sufficientlysmall so as to permit only single grains to grow therein. Each one ofthe at least one metal layer strip is irradiated by a first radiationbeam pulse having an intensity pattern that includes a plurality ofregularly spaced, relatively narrow, linear, stripe-like shadow regions,and a plurality of regularly spaced, relatively wide, linear,stripe-like beamlets. Each one of the beamlets is positioned in betweenand adjoining respective adjacent shadow regions. Each segment of eachone of the at least one metal layer strip is diagonally oriented withrespect to the shadow regions and the beamlets. When each one of the atleast one metal layer strip is irradiated by the first radiation beampulse, each region of the metal layer strip overlapped by a respectiveone of the beamlets is melted throughout its entire thickness, and eachregion of the at least one metal layer strip overlapped by a respectiveone of the shadow regions remains at least partially unmelted. Each atleast partially unmelted region adjoins respective adjacent meltedregions. Following irradiation by the first radiation beam pulse, eachmelted region of each one of the at least one metal strip is permittedto cool and resolidify. During resolidification of each melted region,different single grains grow from each at least partially unmeltedregion in each adjoining melted region, and in each melted regionrespective single grains grow from adjoining at least partially unmeltedregions in opposite directions towards one another, and abut one anotherat a respective one of a plurality of first grain abutment boundariesafter the abutting single grains have grown by an abutting grain growthdistance. Each one of the first grain abutment boundaries isapproximately parallel to the shadow regions and the beamlets. Aftercompletion of resolidification of each melted region of each one of theat least one metal layer strip following irradiation by the firstradiation beam pulse, each one of the at least one metal layer strip isirradiated by a second radiation beam pulse having the same intensitypattern as the first radiation beam pulse, but where the shadow regionsand beamlets thereof are each shifted in a direction perpendicular tothe first grain abutment boundaries by a distance at least equal to thewidth of the shadow regions but less than the distance that would causethe shifted shadow regions to overlap the first grain boundaries. Wheneach one of the at least one metal layer strip is irradiated by thesecond radiation beam pulse, each region of each one of the at least onemetal layer strip overlapped by a respective one of the shifted beamletsis melted throughout its entire thickness, and each region of the atleast one metal layer strip overlapped by a respective one of theshifted shadow regions remains at least partially unmelted. Each atleast partially unmelted region adjoins respective adjacent meltedregions. After irradiation by the second radiation beam pulse, eachmelted region of each one of the at least one metal layer strip ispermitted to cool and resolidify. During resolidification of each meltedregion, a respective single grain grows from each at least partiallyunmelted region in each adjoining melted region, and in each meltedregion, respective single grains grow from adjoining at least partiallyunmelted regions in opposite directions towards one another, and abutone another at a respective one of a plurality of second grain abutmentboundaries after the abutting single grains have grown by the abuttinggrain growth distance. Each one of the second grain abutment boundariesis approximately parallel to the shifted shadow regions and the shiftedbeamlets. After completion of resolidification of each melted regionfollowing irradiation by the second radiation beam pulse, each one ofthe at least one metal layer strip has a grain structure comprisingregions of single grains extending between respective adjacent secondgrain abutment boundaries. Each second grain abutment boundary isperpendicularly oriented in relation to a respective one of the at leastone metal layer strip at the location of the second grain abutmentboundary.

According to a ninth exemplary embodiment of the method of the presentinvention, the metal layer is irradiated by a first radiation beam pulsehaving an intensity pattern that includes at least one stripe-shapedbeamlet each having a respective one of at least one predefined contour.Each region of the metal layer overlapped by a respective one of the atleast one beamlet is melted throughout its entire thickness so as toform at least one stripe-shaped melted region having a respective one ofthe at least one predefined contour, and each region of the metal layernot overlapped by a respective one of the at least one beamlet remainsat least partially unmelted. Each one of the at least one melted regionadjoins at least one adjacent at least partially unmelted region along afirst and a second edge of the melted region. After irradiation by thefirst radiation beam pulse, each one of the at least one melted regionis permitted to cool and resolidify. During resolidification of each oneof the at least one melted region, first and second rows of grains growtherein from the first and second edges thereof, respectively, inopposite directions towards one another until each one of the first andsecond rows of grains has grown by an abutting grain growth distance.After each one of the at least one melted region has completelyresolidified to form at least one resolidified region each having arespective one of the at least one predefined contour, the metal layeris patterned to form at least one relatively narrow metal strip from arespective strip-shaped region in one of the first and second rows ofgrains in each one of the at least one resolidified region. Each one ofthe at least one metal layer strip has a respective one of the at leastone predefined contour and regions of single grains separated by grainboundaries each forming a relatively large angle with a respective oneof the at least one metal layer strip at the location of the grainboundary.

According to a tenth embodiment of the method of the present invention,the metal layer is divided for processing purposes into a plurality ofcolumns having a predetermined width. A first column of the metal layeris irradiated in a first pass by a pulsed radiation beam having apredetermined pulse repetition rate by translating the substrate havingthe metal layer at a predetermined translation velocity past theposition of impingement of the pulsed radiation beam on the metal layerso that the pulsed radiation beam scans the entire length of the firstcolumn. Each pulse of the pulsed radiation beam has an intensity patternthat includes at least one shadow region and at least one beamlet, theintensity pattern having a width at least equal to the predeterminedwidth of the columns. During each pulse of the pulsed radiation beam,each region of the metal layer overlapped by a respective one of the atleast one beamlet is melted throughout its entire thickness, and eachregion of the metal layer overlapped by a respective one of the at leastone shadow region remains at least partially unmelted. Each at leastpartially unmelted region adjoins at least one adjacent melted region.The predetermined translation velocity of the substrate having the metallayer and the preselected pulse repetition rate of the pulsed radiationbeam are chosen so that each melted region in a previous portion of themetal layer irradiated by a previous pulse of the pulsed radiation beamcompletely solidifies before a next portion which overlaps the previousportion is irradiated by a next pulse of the pulsed radiation beam.After the first column has been irradiated by the pulsed radiation beamin the first pass, the intensity pattern of each pulse of the pulsedradiation beam is shifted with respect to the intensity pattern of thepulses of the pulsed radiation beam in the first pass by shifting thesubstrate having the metal layer by a relatively small distance in adirection perpendicular to the columns. After shifting of the metallayer, the first column is irradiated in a second pass by a pulsedradiation beam having the preselected pulse repetition rate and theshifted pulse intensity pattern by translating the substrate having themetal layer at the predetermined translation velocity past the positionof impingement of the pulsed radiation beam on the metal layer so thatthe pulsed radiation beam scans the entire length of the first column inthe second pass. The shifting of the metal layer and the irradiation ofthe first column in a next pass is repeated, if needed, until a desiredgrain structure is obtained in the first column. Thereafter, thesubstrate having the metal layer is translated in a lateral directionperpendicular to the columns so that the pulsed radiation beam ispositioned to irradiate a second column in a first pass. Following thelateral translation step, the steps of irradiating the second column ina first pass, shifting the metal layer, irradiating the second column ina second pass, and continuing, if needed, the shifting of the metallayer and the irradiating of the second column in a next pass arecarried out in combination until a desired grain structure is obtainedin the second column. Thereafter, the steps of laterally translating themetal layer, irradiating a next column in a first pass, shifting of themetal layer, irradiating the next column in a second pass, andcontinuing, if needed, the shifting of the metal layer and theirradiating of the next column in a next pass are repeated incombination until the desired grain structure is obtained in each columnof the metal layer.

In accordance with the method of the present invention, the metal layermay be subdivided for processing purposes into a plurality of sections,and the method steps of the present invention may be carried out incombination in each of the sections one at a time. Alternatively, themethod steps may be carried out one step at a time in each section oneat a time until all of the method steps of the method have been carriedout in all of the sections of the metal layer.

In accordance with another aspect of the present invention, there isprovided an apparatus for processing a metal layer on the substratecomprising a pulsed radiation beam source for providing radiation beampulses and a beam mask through which the radiation beam passes fordefining a respective intensity pattern of each one of the radiationbeam pulses for irradiating at least a portion of the metal layer. Therespective intensity pattern of each one of the radiation beam pulseshas at least one shadow region and at least one beamlet, wherein duringirradiation by a radiation beam pulse, each region of the metal layeroverlapped by a respective one of the at least one beamlet is meltedthroughout its entire thickness, and each region of the metal layeroverlapped by a respective one of the at least one shadow region remainsat least partially unmelted. Also included in the apparatus is a sampletranslation stage for holding the substrate having the metal layer whileat least a portion of the metal layer is being irradiated by a radiationbeam pulse, and for translating the substrate having the metal layer ina lateral direction with respect to the pulsed radiation beam. Thesample translation stage may be used to microtranslate the metal layeron the substrate in a lateral direction with respect to the radiationbeam pulses so as to shift the intensity pattern of the radiation beampulses with respect to the metal layer from one pulse to another.

According to an exemplary embodiment of the apparatus of the presentinvention, the pulsed radiation beam source is a pulsed excimer laser,and the apparatus includes a first optical path traversed by theradiation beam pulses from the excimer laser to the beam mask, which maybe a projection mask, a proximity mask or a contact mask. According toanother exemplary embodiment of the present invention, the beam mask isa projection mask mounted in a mask translation stage so that the maskmay be translated with respect to the laser beam pulses passingtherethrough. In accordance with the further exemplary embodiment of theapparatus of the present invention, the beam mask is a projection mask,and the first optical path includes a controllable beam energy densitymodulator, a variable attenuator, beam expanding and collimating lenses,a beam homogenizer, a condenser lens, a field lens, and at least onebeam steering mirror. According to yet another exemplary embodiment ofthe apparatus of the present invention, the apparatus includes a secondoptical path traversed by the radiation beam pulses from the beam maskto the metal layer on the substrate on the sample translation stage. Thesecond optical path includes an eye piece, a controllable shutter, anobjective lens and at least one beam steering mirror. In a still furtherexemplary embodiment of the apparatus in accordance with the presentinvention, the apparatus includes a computer for controlling at leastthe excimer laser, the variable attenuator and the sample translationstage.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments of the present invention will now be described indetail with reference to the accompanying drawings in which:

FIG. 1A is a schematic diagram of an exemplary embodiment of anapparatus for performing lateral solidification (“LS”) processing ofthin metal layers according to the present invention;

FIG. 1B is a cross sectional view of a portion of a first exemplarysample having a thin metal layer disposed on a substrate having adiffusion barrier layer;

FIGS. 2A–2I illustrate the radiation beam pulse intensity pattern andthe grain structure of relatively narrow metal layer strips at differentstages of LS processing in accordance with a first exemplary embodimentof the method of the present invention;

FIGS. 3A–3E illustrate the radiation beam pulse intensity pattern andthe grain structure of relatively narrow metal layer strips at differentstages of LS processing according to a second exemplary embodiment ofthe method of the present invention;

FIG. 4A is a cross sectional view of a second exemplary sample having athin metal layer disposed in a groove of a substrate having a diffusionbarrier layer;

FIG. 4B is a plan view of the second exemplary sample of FIG. 4A;

FIG. 4C is an isometric view of the second exemplary sample of FIG. 4A;

FIG. 5 is a flow diagram representing exemplary LS processing under atleast partial computer control according to the method of the presentinvention as may be carried out by the apparatus of FIG. 1A;

FIG. 6A–6F illustrate the radiation beam pulse intensity pattern and thegrain structure of a portion of a metal layer at different stages of LSprocessing according to a third exemplary embodiment of the method ofthe present invention in which the intensity pattern of the radiationbeam pulses has an array of relatively small, dot-like shadow regions;

FIGS. 7A–7H illustrate the radiation beam pulse intensity pattern andthe grain structure of a portion of a metal layer at different stages ofLS processing according to a fourth exemplary embodiment of the methodof the present invention, in which the intensity pattern of theradiation beam pulses has beamlets in the form of regularly spaced,repeating chevrons where adjacent repeating chevron-shaped beamlets arestaggered with respect to one another;

FIGS. 8A–8D illustrate the radiation beam pulse intensity pattern andthe grain structure of a portion of a metal layer at various stages ofLS processing according to a fifth exemplary embodiment of the method ofthe present invention, in which the intensity pattern of the radiationbeam pulses has regularly spaced, relatively narrow, linear, stripe-likeshadow regions, and regularly spaced, relatively wide, linear,stripe-like beamlets, each one of the beamlets being positioned inbetween and adjoining respective adjacent ones of the shadow regions;

FIGS. 9A and 9B illustrate the radiation beam pulse intensity patternand metal layer grain structure obtained using a variation of the fifthexemplary embodiment of the method of the present invention, in whichthe shadow regions and the beamlets of the radiation beam pulseintensity pattern are oriented diagonally with respect to the X and Ydirections to obtain diagonally oriented grains that extend betweenrespective adjacent grain abutment boundaries;

FIGS. 10A–10E illustrate the radiation beam pulse intensity pattern andthe grain structure of a portion of a metal layer at various stages ofLS processing according to a sixth exemplary embodiment of the method ofthe present invention, the sixth exemplary embodiment being an extensionof the fifth exemplary embodiment;

FIGS. 11A–11D illustrate the radiation beam pulse intensity pattern andthe grain structure of a metal layer strip at various stages of LSprocessing according to a seventh exemplary embodiment of the method ofthe present invention, in which the intensity pattern of the radiationbeam pulses has a plurality of relatively narrow, linear, stripe-likeshadow regions overlapping the metal layer strip at regular intervalsarid a beamlet overlapping all regions of the metal layer strip notoverlapped by the shadow regions;

FIGS. 12A–12D illustrate the radiation beam pulse intensity pattern andthe grain structure of a metal layer strip having a right angle bend atvarious stages of LS processing according to an eighth exemplaryembodiment of the method of the present invention, in which theintensity pattern of the pulsed radiation beam has regularly spaced,relatively narrow, linear, stripe-like shadow regions and regularlyspaced relatively wide, linear, stripe-like beamlets, each one of thebeamlets being positioned in between and adjoining respective adjacentshadow regions, each segment of the metal layer strip being orienteddiagonally with respect to the shadow regions and beamlets;

FIGS. 13A–13C illustrate different stages of formation of a metal layerstrip having single grain regions separated by grain boundaries that areat large angles with respect to the metal layer strip at respectivelocations of the grain boundaries according to a ninth exemplaryembodiment of the method of the present invention;

FIG. 14 illustrates a metal layer undergoing continuous LS processingaccording to a tenth exemplary embodiment of the method of the presentinvention, where for simplicity of the depiction the positions andirradiation paths of the stationary pulsed radiation beam are shown inthe frame of reference of the translating sample;

FIGS. 15A–15G illustrate an exemplary radiation beam pulse intensitypattern and the grain structure of a portion of a column of the metallayer depicted in FIG. 14 at different stages LS processing according tothe tenth exemplary embodiment of the method of the present invention;and

FIGS. 16A–16G are diagrams depicting subdividing a metal layer intosections for processing purposes and carrying out LS processing of themetal layer in accordance with the present invention on asection-by-section basis.

DETAILED DESCRIPTION

Referring to FIG. 1A, there is shown an exemplary embodiment of anapparatus for carrying out LS processing of thin metal layers accordingto the present invention. The exemplary apparatus includes a LambdaPhysik model LPX-315I XeCl pulsed excimer laser 110, a MicroLastwo-plate variable attenuator 130, beam steering mirrors 140, 143, 147,160 and 162, beam expanding and collimating lenses 141 and 142, aMicroLas beam homogenizer 144, a condenser lens 145, a field lens 148, aprojection mask 150 which may be mounted in a translating stage (notshown), a 4×–6× eye piece 161, a Vincent Associates UniBlitz Model D122controllable shutter 152, a multi-element objective lens 163 forfocusing an incident radiation beam pulse 164 onto a sample 40 having athin metal layer 52 to be LS processed mounted on a sample translationstage 180, a granite block optical bench 190 supported on a vibrationisolation and self-leveling system 191, 192, 193 and 194, and aCyberResearch Inc. Industrial Computer System (with a Pentium processor3 running Windows ME) computer 106 coupled to control the pulsed excimerlaser 110, the beam energy density modulator 120, the variableattenuator 130, the shutter 152 and the sample translation stage 180.The sample translation stage 180 is controlled by the computer 106 tomake translations and/or microtranslations of the sample 40 in the X, Yand Z directions. It will be understood by those skilled in the art thatinstead of a pulsed excimer laser, the pulsed radiation beam source 110may be another known source of short energy pulses suitable for meltinga thin metal layer in the manner described hereinbelow, such as a pulsedsolid state laser, a chopped continuous wave laser, a pulsed electronbeam or a pulsed ion beam, etc. with appropriate modifications to theradiation beam path from the source 110 to the sample 40. While thecomputer 106 in the exemplary apparatus embodiment of FIG. 1A controlsmicrotranslations of the sample 40 for carrying out LS processing of ametal layer 52, the computer may also be adapted to controlmicrotranslations of the mask 150 mounted in an appropriate masktranslation stage (not shown) to shift the intensity pattern of theradiation beam pulses with respect to the metal layer 52. The exemplaryapparatus of FIG. 1A may be used to carry out LS processing of a metallayer 52 on a sample 40 in the manner to be described.

Turning to FIG. 1B, there is shown a cross-sectional view of anexemplary sample 40. The sample 40 comprises a substrate 50 having adiffusion barrier layer 51and a metal layer 52 overlying the diffusionbarrier layer. The substrate 50 may be a semiconductor substrate havingpartially or wholly fabricated integrated circuit devices therein. Themetal layer 52 may be a multiplicity of metal interconnect lines of oneor more integrated circuit devices, or a continuous metal layer beforebeing patterned into such interconnect lines or for use in otherapplications. The diffusion barrier layer 51 may be a layer of SiO₂, alayer of Tantalum (Ta), a layer of a composition which includes Ta or ofany other suitable material which prevents diffusion of the material ofmetal layer 52 into the underlying substrate 50 and which permits thelateral growth of metal grains thereon. It is noted that the diffusionbarrier or any substrate surface on which the metal layer 52 is disposedmust not seed growth of grains in the metal layer 52.

The metal layer 52 is deposited on the diffusion barrier layer 51 of thesubstrate 50 using conventional techniques, for example, a CVD (ChemicalVapor Deposition) process, a PVD (Physical Vapor Deposition) process oran electrochemical deposition, all of which are known to those skilledin the art. The metal layer 52 may consist of any elemental metal,compound metal or alloy, such as aluminum, copper, tungsten, titanium,platinum or gold, suitable for forming interconnect lines in integratedcircuit devices or suitable for use in other applications. In addition,the material of the diffusion barrier layer 51 is advantageouslyselected so that when the metal layer 52 is melted, the melted metalwill “wet” the surface of the diffusion barrier layer 51 appropriately.Such “wetting” allows the metal layer 52 when melted to remain uniformlydisposed on the diffusion barrier layer 51, and thereby preventsagglomeration of the molten metal layer 52. However, “wetting” of thediffusion barrier layer 51 by the metal layer 52 when melted is not anecessity since agglomeration may be avoided by using shorter radiationbeam pulses (e.g., having a pulse duration of less than 30 nsec) to meltthe metal layer 52.

A first exemplary embodiment of the method of the present invention isnow described with reference to FIGS. 2A–2I. As shown in FIG. 2A, anexemplary region of a sample 40, such as a partially fabricatedintegrated circuit device, has three thin metal layer strips 80, 81, 82collectively comprising the metal layer 52. These metal layer strips 80,81, 82, which are formed of copper, for example, by conventional metaldeposition, and conventional patterning by photolithography and etching,have small grains and grain boundaries randomly oriented in variousdirections therein. The widths of the metal layer strips 80, 81, 82 aretypically in the range of 0.1 μm to 10 μm, and the thickness of themelted layer strips is typically in the range of less than 0.1 μm to 1μm. It should be understood that the metal layer 52 being processed mayinclude the metal interconnect lines of an entire partially fabricatedintegrated circuit device or of multiple partially fabricated integratedcircuits on a semiconductor wafer as the sample 40. In practice, thenumber of metal interconnect lines in a given metal level of an entiremodem VLSI integrated circuit device can be on the order of tens ofthousands or greater. In addition, these interconnect lines can extendfor lengths that are much longer than the lengths of the exemplary metallayer strips shown in FIGS. 2A–2I.

As discussed above, having small grains and randomly oriented grainboundaries is undesirable from the standpoint of electromigration, andmay lead to an undesirably high rate of failure in one or more of thesemetal layer strips 80, 81, 82 when used as interconnect lines forcarrying high current densities. The interconnect lines of an integratedcircuit device generally have a “Manhattan geometry”, i.e., eachinterconnect line is either straight or changes direction only at a 90°angle with respect to an adjoining segment of the interconnect line. Itis noted that the LS process of the present invention is equallyapplicable for processing metal layer strips that change directions atangles other than 90° with respect to adjoining segments of the metallayer strips, or where the metal layer strips have curved contours.

Referring to FIG. 2B there is shown the metal layer strips 80, 81, 82after being irradiated with a first radiation beam pulse having adesired intensity pattern. In the present exemplary embodiment, theradiation beam pulse is a XeCl excimer laser beam pulse having awavelength of 308 nm. Referring to FIG. 1A, the radiation beam pulse isgenerated by an excimer laser 110, and a mask 150 is used to define thedesired intensity pattern of the radiation beam pulse. As shown in FIG.2B, the intensity pattern of the first radiation beam pulse, as definedby the mask 150, includes respective series of multiple, regularlyspaced, dot-like “shadow regions” 61, in which the beam intensity istotally blocked by the mask 150 so as to prevent irradiation of regionsoverlapped by respective ones of the shadow regions 61 in each of metallayer strips 80, 81, 82. For the first radiation beam pulse the dot-likeshadow regions 61 of each series overlap a respective one of the metallayer strips 80, 81, 82 at regular intervals along the centerlinethereof. The intensity pattern of the first radiation beam pulse alsoincludes a “beamlet” having full radiation beam intensity andoverlapping all regions of the metal layer strips 80, 81, 82 notoverlapped by a respective one of the shadow regions 61.

When the metal layer strips 80, 81, 82 are irradiated by the firstradiation beam pulse having the intensity pattern defined by the mask150, each region of the metal layer strips 80, 81, 82 overlapped by thebeamlet is melted throughout its entire thickness, while each region ofthe metal layer strips 80, 81, 82 overlapped by a respective one of theshadow region 61 remains at least partially unmelted and therefore hasthe original grain structure of the metal layer strips 80, 81, 82 asthey were formed. The shadow regions 61, which may have any shape, suchas a circle, a square, etc., have a small area, but are large enough sothat thermal diffusion from the surrounding melted metal layer does notresult in complete melting of the regions overlapped by respective onesof the shadow regions 61. In accordance with the invention, the regionsoverlapped by respective ones of the shadow regions must remain at leastpartially unmelted. Typically, the radiation beam pulses from theexcimer laser 110 provide a beamlet intensity in the range of 10 to 10⁴mJ/cm², a pulse duration (FWHM) in the range of 10 to 10³ nsec, and apulse repetition rate in the range of 10 Hz to 10⁴ Hz. Subject to theenergy limitations of the radiation beam pulses provided by the pulsedexcimer laser 110 in the apparatus of FIG. 1A, the intensity pattern ofthe radiation beam pulses defined by the mask 150 may irradiate all ofthe metal interconnect lines of an entire partially fabricatedintegrated circuit device, all of the metal interconnect lines ofmultiple partially fabricated integrated circuit devices or all of themetal interconnect lines of all partially fabricated integrated circuitdevices on an entire wafer.

Turning to FIG. 2C, after the metal layer strips 80, 81, 82 areirradiated by the first radiation beam pulse, the melted regions of themetal layer strips 80, 81, 82 are permitted to cool and resolidify.Since the at least partially unmelted regions 63 have the original grainstructure of the metal layer strips 80, 81, 82, such grain structure ineach at least partially unmelted region 63 seeds lateral growth ofgrains into adjoining resolidifying melted regions of metal layer strips80, 81, 82. During such resolidification of each melted region, grainsgrow outward from each one of the at least partially unmelted regions 63in a respective resolidification region 55 immediately surrounding theat least partially unmelted region 63 in each one of the metal layerstrips 80, 81, 82. Each resolidification region 55 is bounded by theedges of a respective one of the metal layer strips 80, 81, 82 and bythe abutment of grains growing from the at least partially unmeltedregion 63 within the resolidification region 55 with grains growing fromadjacent at least partially unmelted regions 63. The abutting graingrowth distance of grains growing from each one of the at leastpartially unmelted regions 63 before abutting grains growing fromadjacent at least partially unmelted regions is approximately half thewidth of the melted regions as defined by the width of the beamlets. Inthis manner, larger grains 62 are formed in each of the resolidificationregions 55 after resolidification of the melted regions of the metallayer strips 80, 81, 82 is completed. The spacing between adjacentshadow regions 61 should be such that grains growing from each at leastpartially unmelted region 63 overlapped by a respective one of theshadow region 61 abuts grains growing from its two adjacent at leastpartially unmelted regions 63 before resolidification of the meltedregions of the metal layer strips 80, 81, 82 is completed (i.e., beforenucleation of new grains occurs in the intervening spaces). Thecharacteristic growth distance of the grains is the distance that thegrains grow before nucleation of new grains occurs.

Where the widths of the interconnect line segments 80, 81, 82 are solarge that growth of grains from the at least partially unmelted regions63 do not reach the edges of the metal layer strips and/or do not abutgrains growing from adjacent at least partially unmelted regions beforethe melted regions therein completely resolidifies, the mask 150 mustdefine an intensity pattern having an appropriate array of shadowregions spaced sufficiently close to respective edges of the metal layerstrips 80, 81, 82 and sufficiently close to each other so that grainsgrowing from each at least partially unmelted region overlapped by arespective one of the shadow regions either reaches an edge of arespective one of the metal layer strips 80, 81, 82, or abuts grainsgrowing from adjacent at least partially unmelted regions beforeresolidification of the melted regions is completed.

Turning now to FIG. 2D, because the position of impingement of thepulsed radiation beam 164 on the metal layer strips 80, 81, 82 ispreferably fixed, the sample 40 is then repositioned by the sampletranslation stage 180 under the control of the computer 106 so that theshadow regions 64 of the intensity pattern of the second radiation beampulse are each slightly shifted by a distance less than the largestabutting grain growth distance after the first radiation beam pulse withrespect to the positions on the metal layer strip of the shadow regions61 of the intensity pattern of the first radiation beam pulse. Theabutting grain growth distance is the distance that a grain grows froman at least partially unmelted region in an adjoining melted regionbefore abutting another grain growing in the same melted region andbefore abutting an edge of the melted layer. In this manner, each shadowregion 64 overlaps a different region within the same resolidificationregion 55 formed after irradiation by the first radiation beam pulse.For example, the position of the new shadow regions 64 is shifted fromthe previous position of the shadow regions 61 by a distance in therange of 0.01 μm to 10 μm. Such minute repositioning shall be referredto hereinafter as a “microtranslation”. Optionally, the mask 150 may bemicrotranslated instead of the sample 40 to obtain the desired shift ofthe shadow regions 64 of the intensity pattern of the second radiationbeam pulse. Although the beamlet of the intensity pattern of the secondradiation beam pulse is also shifted with respect to that of theintensity pattern of the first radiation beam pulse, the shifted beamletstill overlaps all regions of the metal layer strips 80, 81, 82 notoverlapped by a respective one of the shifted shadow regions 64.

As shown in FIG. 2D, after the above-described microtranslation of thesample 40, the apparatus of FIG. 1A irradiates the metal layer strips80, 81, 82 with a second radiation beam pulse, so that each region ofthe metal layer strips 80, 81, 82 overlapped by the shifted beamlet ismelted throughout its entire thickness, and each region of the metallayer strips overlapped by a respective one of the shifted shadowregions 64 remains at least partially unmelted. Each one of the at leastpartially unmelted regions adjoins respective adjacent melted regions.The sample 40 may be microtranslated in any direction so long as eachone of the shifted shadow regions 64 overlaps a region within the sameresolidification region 55 as a region overlapped by a corresponding oneof the shadow regions 61 of the intensity pattern of the first radiationpulse. For example, the sample 40 can be microtranslated in the −Adirection which is at minus 135° with respect to the X axis, whererotation of angles in the counterclockwise direction are taken aspositive, or the sample can be microtranslated in the +A direction whichis at an angle of 45° with respect to the X axis.

Referring to FIG. 2E, there are shown the metal layer strips 80, 81, 82after completion of resolidification of the melted regions followingirradiation by the second radiation beam pulse. Because each one of theat least partially unmelted regions 65 after the first microtranslationof the sample 40 and the irradiation by the second radiation beam pulsecontains a smaller number of grains than was contained in each one ofthe at least partially unmelted regions 63 after irradiation by thefirst radiation beam pulse, there will be an equal to greater number ofgrains that will be grown in a corresponding one of new resolidificationregions 55′ upon resolidification of each melted region of the metallayer strips 80, 81, 82 after irradiation by the second radiation beampulse. As illustrated in FIG. 2E, growth of the grains takes placelaterally from each of the shifted at least partially unmelted regions65 to either reach an edge of a respective one of the metal layer strips80, 81, 82, or to abut grains growing from adjacent shifted at leastpartially unmelted regions 65 to define the new resolidification regions55′, the abutting grains having grown by respective abutting growthdistances. Referring to FIG. 2E, each of the new resolidificationregions 55′ has fewer and larger grains 66 than the previousresolidification regions 55 illustrated in FIG. 2C.

Referring to FIG. 2F, after resolidification of the melted regionsfollowing irradiation by the second radiation beam pulse is completed,the sample 40 may be further microtranslated with respect to the pulsedradiation beam 164 in any direction by a distance less than the largestabutting grain growth distance after the second radiation beam pulse sothat the twice-shifted shadow regions 67 of the intensity pattern of athird radiation beam pulse each overlaps a different region within arespective one of the resolidification regions 55. In the exemplaryembodiment illustrated in FIG. 2F the direction of the furthermicrotranslation B is at 45° with respect to the X axis. After thesample 40 is microtranslated in this direction, the metal layer strips80, 81, 82 are irradiated by the third radiation beam pulse having thesame intensity pattern defined by the mask 150, but where the shadowregions 67 have each been shifted twice. The twice-shifted shadowregions 67 are displaced from respective previous shadow regions 64 by adistance less than the largest abutting grain growth distance after thesecond radiation beam pulse, for example, in the range of 0.01 μm to 10μm. Although the beamlet of the intensity pattern of the third radiationbeam pulse is also shifted with respect to that of the intensity patternof the second radiation beam pulse, the twice-shifted beamlet stilloverlaps all regions of the metal layer strips 80, 81, 82 not overlappedby a respective one of the twice-shifted shadow regions 67.

With reference to FIG. 2G, there are illustrated the resolidified metallayer strips 80, 81, 82 after irradiation by the third radiation beampulse and completion of resolidification of the melted regions. Becausethe twice-shifted at least partially unmelted regions 71 each contain asmaller number of grains than was contained in the once-shifted at leastpartially unmelted regions 65, there will be an equal or smaller numberof grains that will be grown in a corresponding one of newresolidification regions 69 upon completion of resolidification of eachmelted region of the metal layer strips 80, 81, 82 after irradiation bythe third radiation beam pulse. As illustrated in FIG. 2G, the growth ofgrains takes place laterally from each of the twice shifted at leastpartially unmelted regions 71 to either reach an edge of a respectiveone of the metal layer strips 80, 81, 82 or to abut grains growing fromadjacent twice shifted at least partially unmelted regions 71 to definethe new resolidification regions 69, the abutting grains having grown byrespective abutting grain growth distances. Referring to FIG. 2G, eachone of the new resolidification regions 69 has fewer and larger grains68 than the previous resolidification regions 55′ illustrated in FIG.2E.

Turning now to FIG. 2H, after resolidification of each melted regionfollowing irradiation by the third radiation beam pulse region iscompleted, the sample 40 may be further microtranslated with respect tothe pulsed radiation beam 164 in any direction by a distance less thanthe largest abutting grain growth distance after the third radiationbeam pulse so that the thrice-shifted shadow regions 63 of the intensitypattern of a fourth radiation beam pulse each overlap a different regionwithin a respective one of the resolidification regions 69. In theexemplary embodiment illustrated in FIG. 6H, the direction of furthermicrotranslation C is at −135° with respect to the X axis, and thedistance of the further microtranslation is in the range of 0.01 μm to10 μm. After the sample 40 is microtranslated in this direction by thisdistance, the metal layer strips 80, 81, 82 are irradiated by the fourthradiation beam pulse having the same intensity pattern as that of thethird radiation beam pulses illustrated in FIG. 2F, but where the shadowregions 72 and the beamlet have each been shifted three times withrespect to the metal layer strips 80, 81, 82.

With reference to FIG. 2I, there is shown the resolidified metal layerstrips 80, 81, 82 after irradiation by the fourth radiation beam pulseand completion of resolidification of each melted region. Because the atleast partially unmelted regions 73 overlapped by respective ones of thethrice-shifted shadow regions 63 (i.e., the thrice-shifted at leastpartially unmelted regions) each contain a single grain, there will bean equal or greater number of grains that will be grown in acorresponding one of the new resolidification regions 70 upon completionof resolidification of the melted regions of the metal layer strips 80,81, 82. As illustrated in FIG. 2I, the growth of grains takes placelaterally from each one of the thrice-shifted at least partiallyunmelted regions 73 to either reach an edge of a respective one of themetal layer strips 80, 81, 82 or to abut the grains growing fromadjacent thrice-shifted at least partially unmelted regions 73 to definethe new resolidification regions 70. As shown in FIG. 2I, each one ofthe new resolidification regions 70 of the metal layer strips 80, 81, 82is a single grain, and each grain boundary is substantiallyperpendicular to a respective one of the metal layer strips 80, 81, 82at the location of the grain boundary. Accordingly, if the metal layerstrips 80, 81, 82 are interconnect line portions of an integratedcircuit device, electromigration in these interconnect line portions issubstantially reduced. It is noted that the metal layer strips 80, 81,82 may be subjected to more or fewer microtranslation, irradiation andresolidification steps, as described with reference to FIGS. 2A–2I, soas to obtain the desired grain structure illustrated in FIG. 2I in eachone of the metal layer strips.

After completion of the above-described LS processing to obtain adesired grain structure in each one of the metal layer strips 80, 81,82, the sample 40 may be translated to a next section for LS processingtherein. A new mask 150 (shown in FIG. 1A) will be required for LSprocessing if the next section has a different configuration of metallayer strips since the series of shadow regions of the intensity patternof the radiation beam pulses, as defined by the mask 150, must conformto the contours of the respective metal layer strips.

A second exemplary embodiment of the method of the present invention isnow described with reference to FIGS. 3A–3E. For purposes ofillustration, the same configuration of metal layer strips 80, 81, 82used to describe the first exemplary embodiment, as illustrated in FIGS.2A–2I, is used to describe the present embodiment. As in the firstexemplary embodiment, the metal layer strips 80, 81, 82, which are shownin FIG. 3A, are formed of copper, for example, and initially have smallgrains and grain boundaries that are oriented in random directions. Eachone of the metal layer strips has a width typically in the range of 0.1μm to 10 μm and a thickness typically in the range of less than 0.1 μmto 10 μm.

Referring to FIG. 3B, the metal layer strips 80, 81, 82 are irradiatedby a first radiation beam pulse having an intensity pattern, as definedby the mask 150 (shown in FIG. 1A), that includes three relativelynarrow stripe-like shadow regions 83 each having the same predefinedcontour of a respective one of the metal layer strips 80, 81, 82. Inaddition to the shadow regions 83, the intensity pattern of the firstradiation beam pulses, as defined by the mask 150, also includes abeamlet that overlaps all regions of the metal layer strips 80, 81, 82not overlapped by the shadow regions 72. Advantageously, the width ofthe shadow regions 83 is in the range of 0.01 μm to 5 μm. Initially, thesample 40 is positioned so that the shadow regions 72 of the intensitypattern of the first radiation beam pulses overlap respective ones ofthe metal layer strips 80, 81, 82 along the center line of each one ofthe metal layer strips. Upon being irradiated by the first radiationbeam pulse, each region of the metal layer strips 80, 81, 82 overlappedby the beamlet is melted throughout its entire thickness, while eachregion of the metal layer strips overlapped by a respective one of theshadow region 72 remains at least partially unmelted. The shadow regions83 of the intensity pattern of the radiation beam pulses aresufficiently wide so that thermal diffusion from the melted regions 85and 86 in each one of the metal layer strips 80, 81, 82 do notsignificantly melt the regions of the metal layer strips 80, 81, 82overlapped by respective ones of the shadow regions 83. Afterirradiation by the first radiation beam pulse, the at least partiallyunmelted regions 84 in each one of the metal layer strips 80, 81, 82will have the original grain structure of the metal layer strips beforeLS processing.

Turning now to FIG. 3C, upon cooling and resolidification of the meltedregions 85 and 86 in each one of the metal layer strips 80, 81, 82 afterirradiation by the first radiation beam pulse, lateral growth of grainswill occur outwardly from each one of the at least partially unmeltedregions 84 in the metal layer strips 80, 81, 82 to the edges of therespective metal layer strips. In this manner, resolidification regions87, 88 are formed in each one of the metal layer strips 80, 81, 82 witheach one of the resolidification regions 87, 88 having a respective row73, 74 of larger metal grains with grain boundaries oriented at largerangles with respect to the metal layer strip.

Turning now to FIG. 3D, after completion of resolidification of themelted regions 85 and 86 in each one of the metal layer strips 80, 81,82 following irradiation by the first radiation beam pulse, the sample40 is microtranslated in the A direction at −135° with respect to theX-axis, or the mask 150 (shown in FIG. 1A) may be microstranslated inthe A direction at 45° with respect to the X-axis, to cause the shadowregions 76 of the intensity pattern of a second radiation beam pulse tobe shifted so as to overlap respective ones of the upper rows of grains73 in each of the metal layer strips 80, 81, 82. It will be understoodby those skilled in the art that either the sample 40 or the mask 150,or both may be microtranslated so as to cause the shadow regions 76 ofthe second radiation beam pulse to overlap respective ones of the lowerrows of grains 74 in each of the metal layer strips 80, 81, 82. Althoughthe beamlet of the intensity pattern of the second radiation beam pulseis also shifted with respect to that of the intensity pattern of thefirst radiation beam pulse, the shifted beamlet still overlaps allregions of the metal layer strips 80,81, 82 not overlapped by arespective one of the shifted shadow regions 76. Except for the shiftingof the shadow regions 76 and the beamlet, the intensity pattern of thesecond radiation beam pulse is the same as that of the first radiationbeam pulse.

After the microtranslation of the sample 40 or the mask 150, the metallayer strips 80, 81, 82 are irradiated by the second radiation beampulse, so that each region of the metal layer strips 80, 81, 82overlapped by the shifted beamlet is melted throughout its entirethickness, while each region of the metal layer strips overlapped by arespective one of the shifted shadow regions 76 remains at leastpartially unmelted. Each at least partially unmelted region adjoinsadjacent melted regions. Because the at least partially unmelted regionswill contain larger grains with grain boundaries forming larger angleswith respect to the metal layer strips 80, 81, 82 than the grains andgrain boundaries of the original metal layer strips, uponresolidification of the melted regions 77 and 78 in each of the metallayer strips 80, 81, 82, these larger grains will seed growth of grainslaterally in each direction from the at least partially unmelted regions85 towards respective edges of the metal layer strips 80, 81, 82 so thateach one of the metal layer strips will have larger grains with grainboundaries that are oriented at large angles (i.e., close to 90°) withrespect to the metal layer strips at respective locations of the grainboundaries, as illustratively represented in FIG. 3E.

After resolidification of the melted regions 77, 78 followingirradiation by the second radiation beam pulse is completed, additionaliterations of microtranslation of the either the sample 40 or the mask150 in an appropriate direction, irradiation by a further radiation beampulse, and resolidification of each melted region of the metal layerstrips may be carried out to further reduce the number of grains in eachone of the metal layer strips 80, 81, 82 and to have the grainboundaries oriented more consistently at large angles with respect tothe metal layer strip at respective locations of the grain boundaries.In the foregoing exemplary embodiment, each one of the radiation beampulses typically has a beamlet intensity in the range of 10 mJ/cm² to10⁴ mJ/cm², a pulse duration (FWHM) in the range of 10 nsec to 10³ nsec,and a pulse repetition rate in the range of 10 Hz to 10⁴ Hz.

After completion of the LS processing of the metal layer strips 80, 81,82, as described above with reference to FIGS. 3A–3E, the sample 40 maybe translated to a next section of the metal layer for LS processingtherein. If the next section has metal layer strips with a differentconfiguration then that shown in FIGS. 3A–3E, a different mask 150defining shadow regions that conform to the respective predefinedcontours of the metal layer strip or strips of the next section must beused. The required mask for LS processing in accordance with the firstand second exemplary embodiments described above are advantageouslyderived from the mask used to pattern a metal layer to form the metallayer strips, such as by conventional photolithography and etching.

Referring to FIGS. 4A–4C, there are shown different views of a sample 40having a substrate 50, a diffusion barrier layer 51 and a metal layer52. The substrate 50 has a recess or groove 105 which is lined with thediffusion barrier layer 51, and then filled with or covered by a thinmetal layer 52 over the diffusion barrier layer 51 within the recess orgroove 105. As in the case of the sample depicted in FIG. 1B, thediffusion barrier layer 51 may consist of a thin layer of any suitablematerial that prevents the metal from the layer 52 from diffusing intothe underlying substrate 50 on which the metal layer 52 is deposited,and permits lateral growth (but not seeding) of grains in the metallayer 52. The metal layer 52 may consist of any elemental metal,compounds metal or alloy, such as aluminum, copper, tungsten, titanium,platinum or gold. The methods and apparatus according to the presentinvention described above (and to be described below) may be used for LSprocessing of a metal layer 52 on a sample 40, as shown in FIGS. 4A–4C,to control the shape and size of grains, and to control the directionand orientation of grain boundaries in the metal layer 52. The sample 40may be a partially fabricated integrated circuit device, multiplepartially fabricated integrated circuit devices, or all partiallyfabricated integrated circuit devices on an entire wafer.

Referring next to FIG. 5, there is shown a flow diagram of exemplarysteps carried out with the aid of the computer 106 (or other controldevices) for LS processing in accordance with the present invention tocontrol the shape and size of grains, and the location and orientationof grain boundaries in a metal layer, such as that described in thefirst and second exemplary embodiments, and other exemplary embodimentsdescribed hereinbelow. As shown in the flow diagram, in step 1000 thehardware components of the apparatus of FIG. 1A, such as the radiationbeam source 110, the beam energy density modulator 120, the beamattenuator 130 and the shutter 152 are first initialized at least inpart by the computer 106. A sample 40 is loaded onto the sampletranslation stage 180 in step 1005. It should be noted that such loadingmay either be performed manually or automatically using known sampleloading apparatus under the control of the computer 106. Next, thesample translation stage 180 is moved, preferably under the control ofthe computer 106 to an initial position in step 1010. The various otheroptical components of the system are adjusted manually or under thecontrol of the computer 106 for proper focus and alignment in step 1015,if necessary. The radiation beam pulses are then stabilized in step 1020to a desired intensity, pulse duration and pulse repetition rate. Instep 1024, it is determined whether each beamlet of the intensitypattern of each radiation beam pulse has sufficient intensity to melteach region of the metal layer 50 overlapped thereby throughout itsentire thicknesses without substantially melting an adjacent regionoverlapped by a shadow region of the intensity pattern. If under-meltingor over-melting occurs, the attenuator 130 is adjusted so that eachradiation beam pulse has sufficient energy to fully melt the metal layerin irradiated regions without over melting adjoining unirradiatedregions.

In step 1030 the sample is irradiated with the first radiation beampulse having an intensity pattern in proper alignment with the metallayer 52 of the sample 40. In step 1032 the sample is microtranslated toshift the intensity pattern of the next radiation beam pulse in apredetermined direction and by a predetermined distance before thesample 40 is irradiated by a next radiation beam pulse.

In step 1035, it is determined whether LS processing of the metal layer52, or a particular section thereof, has been completed by determiningwhether the sample 40 has undergone a predetermined number ofmicrotranslations. If the sample 40 has not undergone the predeterminednumber of microtranslations, the process loops back to step 1032 for afurther microtranslation to shift the intensity pattern of the nextradiation beam pulse in a predetermined direction and by a predetermineddistance, and irradiation of the sample by the next radiation beampulse. If the sample has undergone the predetermined number ofmicrotranslations, processing proceeds to step 1045. In step 1045 it isdetermined whether there are any more sections of the metal layer for LSprocessing. If there are more sections to be processed, in step 1050 thesample is translated to the next section for LS processing. If there areno more sections of the sample for LS processing, the processterminates.

Referring now to FIGS. 6A–6E, there are shown the radiation beam pulseintensity pattern and the grain structure of the metal layer atdifferent stages of LS processing according to a third exemplaryembodiment of the method of the present invention. As shown in FIG. 6A,the metal layer 52 of the sample 40 is irradiated by a first radiationbeam pulse having an intensity pattern that includes a predeterminedregular array of relatively small, dot-like shadow regions 1200, asdefined by the mask 150 (shown in FIG. 1A). The metal layer 52, which isformed of copper, for example, may be a metal layer deposited on one ormore partially fabricated integrated circuit devices, or a wafer havingmultiple partially fabricated integrated circuit devices before themetal layer is patterned into interconnect lines of the integratedcircuit devices.

Still referring to FIG. 6A, in addition to the array of dot-like shadowregions 1200, which are located at respective intersections of mutuallyorthogonal diagonal lines, the intensity pattern of the first radiationbeam pulse includes a beamlet that overlaps all regions of the metallayer 52, or an entire section thereof, not overlapped by the shadowregions 1200. When the metal layer is irradiated by the first radiationbeam pulse, each region of the metal layer 52 overlapped by the beamletis melted throughout its entire thickness, and each region of the metallayer overlapped by a respective one of the shadow regions 1200 remainsat least partially unmelted. The shadow regions 1200 are sufficientlylarge so that thermal diffusion from the melted regions of the metalfilm 52 does not cause substantial melting of the regions of the metallayer 52 overlapped by the shadow regions 1200. Therefore, the at leastpartially unmelted dot-like regions 1201 shown in FIG. 6B each have thegrain structure of the metal layer 52 as originally formed. The dot-likeshadow regions 1200 may have any shape, such as circular, square,hexagonal, etc. Advantageously, the dot-like shadow regions 1200 arecircular and have a diameter in the range of 1 μm to 10 μm, and anearest neighbor spacing of 2 μm to 100 μm.

Turning to FIG. 6B, there are shown the melted and the at leastpartially unmelted regions of the metal layer 52 as the melted regionsresolidify after irradiation by the first radiation beam pulse. Duringresolidification of each melted region, grains grow laterally from eachone of the at least partially unmelted regions 1201 until such grainsabut other grains growing from adjacent at least partially unmeltedregions 1201 after the abutting of grains have grown by a characteristicgrowth distance, and there are formed approximately square-shaped firstresolidification regions 1220 defined by first grain abutmentboundaries. Respective abutting grain growth distances of the abuttinggrain are defined by the pitch of the shadow regions 1200 (i.e., thenearest neighbor spacings). After completion of resolidification of eachmelted region of the metal layer 52 after irradiation by the firstradiation beam pulse, each resolidification region 1220 has a smallernumber of larger grains than the metal layer 52 as originally formed.

Referring now to FIG. 6C, after completion of resolidification of eachmelted region of the metal layer 52 following irradiation by the firstradiation beam pulse, the sample 40 having the metal layer 52 ismicrotranslated in any direction by a distance less than thecharacteristic growth distance, so that the shadow regions 1240 of theintensity pattern of a second radiation beam pulse are shifted withrespect to corresponding ones of the shadow regions 1200 of theintensity pattern of the first radiation beam pulse so as to overlapdifferent regions within respective ones of the first resolidificationregions 1220. In the example of FIG. 6C, the sample 40 ismicrotranslated by a few micrometers (i.e., less than the abutting graingrowth distance following irradiation by the first radiation beam pulse)in the A direction, which forms an angle of minus 135° with the X axis.Although the beamlet of the intensity pattern of the second radiationbeam pulse is also shifted with respect to the metal layer 52, theshifted beamlet still overlaps all regions of the metal layer 52 notoverlapped by the shifted shadow regions 1240.

After microtranslation of the sample 40, the metal layer 52 isirradiated with the second radiation beam pulse so that each region ofthe metal layer 52 overlapped by the shifted beamlet is meltedthroughout its entire thickness, and each region of the metal layer 52overlapped by a respective one of the shifted shadow regions 1240remains at least partially unmelted. The microtranslation of the metallayer 52 causes the at least partially unmelted regions 1241, shown inFIG. 6D, to contain fewer grains than the at least partially unmeltedregions 1201 after irradiation by the first radiation beam pulse. It isnoted that instead of microtranslating the sample 40, the same intensitypattern of the second radiation beam pulse having the shifted shadowregions 1240 may be obtained by microtranslating the mask 150 (shown inFIG. 1A) while the sample 40 remains stationary. Except for the shiftingof the shadow regions 1240 and the beamlet, the intensity pattern of thesecond radiation beam pulse is the same as that of the first radiationbeam pulse.

Turning now to FIG. 6D, upon resolidification of the melted regions ofthe metal layer 52, grains will grow outwardly from each of the shiftedat least partially unmelted regions 1241 until such grains abut othergrains growing outwardly from adjacent shifted at least partiallyunmelted regions 1241 after the abutting grains have grown by thecharacteristic growth distance, and there are formed approximatelysquare shaped second resolidification regions 1250 defined by respectivesecond grain abutment boundaries. Comparing FIG. 6D to FIG. 6B, themetal layer 52 after completion of resolidification followingirradiation by the second radiation beam pulse has fewer and largergrains than it did after resolidification following irradiation by thefirst radiation beam pulse.

Referring to FIG. 6E, after completion of resolidification followingirradiation by the second radiation beam pulse the sample 40 ismicrotranslated in any direction by a distance less than thecharacteristic growth distance, so that the shadow regions 1250 of theintensity pattern of a third radiation beam pulse are shifted withrespect to corresponding ones of the shadow regions 1240 of theintensity pattern of the second radiation beam pulse by a distance lessthan the characteristic growth distance so as to overlap differentregions within respective ones of the second resolidification regions.In the example of FIG. 6E, the sample 40 is microtranslated by adistance in the range from 1 μm to 100 μm in the −B direction, whichforms an angle of 45° with the X axis. Although the beamlet of theintensity pattern of the third radiation beam pulse is also shifted withrespect to that of the intensity pattern of the second radiation beampulse, the twice-shifted beamlet still overlaps all regions of the metallayer 52 not overlapped by the shifted shadow regions 1250. The metallayer 52 is then irradiated with the third radiation beam pulse, so thateach region of the metal layer 52 overlapped by the twice-shiftedbeamlet 1250 is melted throughout its entire thickness, while eachregion of the metal layer 52 overlapped by a respective one of thetwice-shifted shadow regions 1250 remains at least partially unmelted.Upon resolidification of each melted region of the metal layer 52,grains grow outwardly from each one of the twice-shifted at leastpartially unmelted regions 1251, shown in FIG. 6F, until such grainsabut other grains growing outwardly from adjacent twice-shifted at leastpartially unmelted regions, and there are formed approximatelysquare-shaped third resolidification regions 1260 defined by third grainabutment boundaries. Because microtranslation of the sample 40 causeseach one of the at least partially unmelted regions 1251 to contain onlya single grain, each of the third resolidification areas 1260 has only asingle grain. It is noted once again that instead of microtranslatingthe sample 40, the same intensity pattern of the third radiation beampulse having the twice-shifted shadow regions 1250 (and beamlet) may beobtained by microtranslating the mask 150 (shown in FIG. 1A) while thesample 40 remains stationary. Typically the radiation beam pulses have abeamlet intensity in the range of 10 mJ/cm² to 10⁴ mJ/cm², a pulseduration (FWHM) in the range of 10 nsec to 10³ nsec, and a pulserepetition rate in the range of 10 Hz to 10⁴ Hz.

If the LS-processed metal layer 52 shown in FIG. 6F is patterned to forminterconnect lines of an integrated circuit device, it is advantageousto form the interconnect lines so that the direction of current flow issubstantially perpendicular to third grain abutment boundaries of theresolidification regions 1260 so as to minimize electromigration.

It will be understood by those skilled in the art that the array ofshadow regions of the intensity pattern of the radiation beam pulses, asdefined by the mask 150, need not have the configuration shown in FIGS.6A–6F, but may be an array having a different configuration, in whichcase the resolidification regions will each have a correspondinglydifferent shape. Moreover, additional microtranslations of the sample 40each followed by irradiation of the metal layer 52 by a furtherradiation beam pulse and resolidification of each melted region of themetal layer may be required in order to obtain resolidification regionseach having only a single grain.

Referring to FIGS. 7A–7H, there are shown the radiation beam pulseintensity pattern and the metal layer grain structure at differentstages of LS processing of a metal layer according to a fourthembodiment of the method of the present invention. In FIG. 7A, a metallayer 52, which is formed of copper, for example, on a sample 40 isirradiated by a first radiation beam pulse having an intensity pattern,as defined by the mask 150 (shown in FIG. 1A), having multiple,regularly spaced beamlets 1300 each having the shape of repeatingchevrons (i.e., a sawtooth shape), and multiple shadow regions 1301 eachpositioned in between and adjoining respective adjacent ones of thebeamlets 1300. Adjacent repeating chevron-shaped beamlets 1300 arestaggered with respect to one another such that downward pointing apexesof each repeating chevron-shaped beamlet 1300 are aligned in the Ydirection with a respective ones of upward pointing apexes of adjacentrepeating chevron-shaped beamlets 1300, and upward pointing apexes ofeach repeating chevron-shaped beamlets 1300 are aligned in the Ydirection with respective ones of downward pointing apexes of adjacentrepeating chevron-shaped beamlets 1300. Each beamlet 1300 has sufficientintensity such that each region of the metal layer 52 overlapped by arespective one of the beamlets 1300 is melted throughout its entirethickness, and each region of the metal layer 52 overlapped by arespective one of the shadow regions 1301 remains at least partiallyunmelted. The width W of the repeating chevron-shaped beamlets 1300 ispreferably in the range of 1 μm to 10 μm, and the minimum separation Dbetween adjacent beamlets 1300 is preferably in the range of 1 μm to 10³μm.

Turning now to FIG. 7B, following irradiation by the first radiationbeam pulse, the melted regions of the metal layer 52 are permitted tocool and resolidify. During resolidification of each melted region,grains grow laterally therein from the opposing boundaries of the meltedregion until rows of grains 1315, 1316 growing in opposite directionstowards one another abut one another along a respective one of firstgrain abutment boundaries 1325 extending approximately along the centerline of each melted region to form first resolidification regions 1310.In this manner, each first resolidification region 1310 has an upwardly(in the +Y direction) grown row of grains 1315 and a downwardly (in the−Y direction) grown row of grains 1316 that abut one another after theabutting grains have grown by an abutting grain growth distance, d,defined by the beamlets and shadow regions. In each firstresolidification region 1310, there is a relatively large single grain1317 at each upward pointing apex of the upwardly grown row of grains1315, and a relatively large single grain 1318 at each downward pointingapex of the downwardly grown row of grains 1316.

After completion of resolidification of each melted region of the metallayer 52, the sample 40 is microtranslated downwardly in the verticaldirection (i.e., in the −Y direction) so that the beamlets 1319 andshadow regions 1326 of the intensity pattern of a second radiation beampulse are shifted with respect to the beamlets 1300 and the shadowregions 1301 of the intensity pattern of the first radiation beam pulseso that a respective one of the shifted beamlets 1319 overlaps a portionof the upwardly grown row of grains 1315 in each resolidification region1310. Specifically, the beamlets 1319 and the shadow regions 1326 (inbetween and adjoining respective adjacent beamlets 1319) of theradiation beam pulse are shifted by less than the abutting grain growthdistance, d. The shifted beamlets 1319 are indicated in FIG. 7B bydashed lines. It is noted that the same shifting of the beamlets andshadow regions may be achieved by microtranslating the mask 150 (shownin FIG. 1A) instead of microtranslating the sample 40.

Referring to FIG. 7C, when the metal layer 52 is irradiated by thesecond radiation beam pulse, each region 1322 of the metal layer 52overlapped by a respective one of the shifted beamlets 1319 is meltedthroughout its entire thickness, while each region 1327 overlapped by arespective one of the shadow regions 1326 remains at least partiallyunmelted. Each at least partially unmelted region adjoins respectiveadjacent melted regions. In particular, portions of the upwardly grownrows of grains 1315 of the first resolidification regions 1310overlapped by the shifted shadow regions 1326 remain at least partiallyunmelted, including portions of the single grain regions 1317.

Turning to FIG. 7D, after irradiation of the metal layer 52 by thesecond radiation beam pulse, each melted region 1322 of the metal layer52 is permitted to cool and resolidify to form second resolidificationregions 1320. Each second resolidification region 1320 has a row ofupwardly grown grains 1315 and a row of downwardly grown grains 1316which abut one another along a respective one of second grain abutmentboundaries 1328, extending approximately along the center line of thesecond resolidification region 1320. The abutting of the upwardly growngrains 1315 with the downwardly grown grains 1316 occurs after thegrains have grown by the abutting grain growth distance, d. Becausegrowth of the row of upwardly grown grains 1315 in each one of thesecond resolidification regions 1320 is seeded by the at least partiallyunmelted portion of the row of upwardly grown grains 1315 in the firstresolidification regions 1310, the upwardly grown grains 1315 are largerin size. In particular, the single grain region 1317 at each upwardpointing apex of the row of upwardly grown grains in each one of thesecond resolidification regions 1320 has increased in size.

Referring to FIG. 7D, after the growth of grains in the secondresolidification regions 1320 is completed, the sample 40 (shown in FIG.1A) is again microtranslated in the downward vertical direction (i.e.the −Y direction) such that each one of the beamlets 1329 and the shadowregions 1330 (in between and adjoining respective adjacent beamlets1329) of the intensity pattern of a third radiation beam pulse isshifted with respect to the beamlets 1319 and the shadow regions 1326 ofthe intensity pattern of the second radiation beam pulse by a distanceless than the characteristic growth distance d so that the twice shiftedbeamlets 1329 overlap respective portions of the rows of upwardly growngrains 1315 in the second resolidification regions 1320. After suchmicrotranslation, the metal layer 52 (shown in FIG. 1A) is irradiated bythe third radiation beam pulse so that each region of the metal layer 52overlapped by a respective one of the twice-shifted beamlets 1329 ismelted throughout its entire thickness, and each region of metal layeroverlapped by a respective one of the twice-shifted shadow regions 1330,including respective portions of the rows of upwardly grown grains 1315in the second resolidification regions 1320, remain at least partiallyunmelted. After irradiation of the metal layer 52 by the third radiationbeam pulse, the melted regions are permitted to cool and resolidify soas to form third resolidification regions (not shown), each havingabutting rows of upwardly grown and downwardly grown grains. In each oneof the third resolidification regions (not shown), the upwardly growngrains have become larger in size, including the single-grain regions atrespective upward pointing apexes of the row of upwardly grown grains.

Turning now to FIG. 7E, after a number of microtranslations,irradiations and resolidifications in the manner described above, thesingle-grain region 1317 at each one of the upward pointing apexes ofeach row of upwardly grown grains continues to grow in size and beginsto abut horizontally adjacent (i.e., in the +X and −X directions)single-grain regions 1317. In addition, each one of the single-grainregions 1317 in each one of the resolidification regions extends intoits vertically adjacent resolidification region directly above (i.e., inthe +Y direction). As shown in FIG. 7E, after resolidification iscompleted, the sample is microtranslated in the downward verticaldirection (i.e., the −Y direction) in the manner described above, andshifted beamlets 1324 of the intensity pattern of a next radiation beampulse, which are indicated by dashed lines, overlap respective portionsof the single-crystal regions 1317 and other regions in the manner shownin FIG. 7E.

Referring to FIG. 7F, upon irradiation by the next radiation beam pulse,each region 1331 of the metal layer 52 overlapped by a respective one ofthe shifted beamlets 1324 is melted throughout its entire thickness, andeach region of the metal layer 52 overlapped by a respective one of theshadow regions (in between and adjoining respective adjacent shiftedbeamlets 1324) remains at least partially unmelted. Uponresolidification of each melted region 1331, as shown in FIG. 7G, thesingle-grain regions 1317 grow even larger so as to abut horizontallyadjacent single-grain regions 1317 over longer grain abutment boundaries1321. Moreover, each one of the single-grain regions 1317 extends closerto single-grain regions 1317 in the vertically adjacent direction (i.e.,the +Y direction).

Turning to FIG. 7H, after a number of additional microtranslations,irradiations and resolidifications in the manner described above, eachone of the single-grain regions 1317 grows so as to abut its twovertically adjacent (i.e., the +Y direction) single-grain region 1317.When each one of the single-grain regions 1317 has grown to fully abutits vertical adjacent single grain regions 1317, the metal layer 52processed in the foregoing manner consists of fully abuttingsingle-grain regions 1317 each having a generally hexagonal shape, asshown in FIG. 7H.

Advantageously, in the foregoing exemplary embodiment, each radiationbeam pulse provides a beamlet intensity in the range of 10 mJ/cm² to 10⁴mJ/cm² with a pulse duration in the region of 10 nsec to 10³ nsec and apulse repetition rate in the range of 10 Hz to 10³Hz.

If the metal layer 52 (shown in FIG. 1A) is to be patterned, it isadvantageously patterned after the above-described LS processing, suchas patterning by conventional photolithography and etching to forminterconnection lines for integrated circuit devices or to form apatterned metal layer for other applications. As mentioned above,instead of microtranslating the sample 40 having the metal film 52, theshifts of the intensity pattern of a next radiation beam pulse withrespect to that of a previous radiation beam pulse may be accomplishedby microtranslating the mask 150 (shown in FIG. 1A) using a conventionalmask translation stage which is not shown. Furthermore, instead ofmicrotranslating the sample 40 or the mask 150 to shift the intensitypattern of a next radiation beam pulse in the upward direction (i.e.,the +Y direction) with respect to the intensity pattern of a previousradiation beam pulse after each irradiation by a previous radiationpulse and resolidification of each melted region of the metal layer, thesame result shown in FIG. 7H may be achieved by microtranslating thesample 40 or the mask 150 to shift the intensity pattern of the nextradiation beam pulse in the downward direction (i.e., the −Y direction)with respect to that of a previous radiation beam pulse after eachirradiation and resolidification.

Referring to FIG. 1A, if LS processing is being carried on a metal layer52 on a section-by-section basis, after completion of the LS processingin the manner described above on a section of the metal layer 52, thesample 40 may be translated to a next section of the metal layer 52 forLS processing in accordance with the foregoing exemplary embodiment.

Referring to FIGS. 8A–8D, there are illustrated the radiation beam pulseintensity pattern and the metal layer grain structure at differentstages of LS processing according to a fifth exemplary embodiment of themethod of the present invention. The metal layer 52 is formed of copper,for example. As shown in FIG. 8A, the intensity pattern of the firstradiation beam pulse, as defined by the mask 150 (shown in FIG. 1A),consists of a plurality of regularly spaced, relatively narrow, linear,stripe-like shadow regions 1401 each extending along the ±Y direction,and a plurality of regularly spaced, relatively wide, linear,stripe-like beamlets 1400 each extending along the ±Y directions. Eachone of the beamlets is positioned in between and adjoining respectiveadjacent shadow regions 1401. The intensity pattern of the firstradiation beam pulse may have any number of shadow regions 1401 andbeamlets 1400 of any length in the ±Y directions, subject to the area ofthe metal layer 52 being processed and the limitation that the radiationbeam pulse must provide sufficient intensity to each beamlet 1400 tomelt a respective metal layer region overlapped by the beamletthroughout the region's entire thickness. Preferably, each one of theshadow regions 1401 has a small width dimension of less than 1 μm to 10μm, and each one of the beamlets 1400 has a small width dimension of 1μm to 10³ μm. When the metal layer 52 is irradiated by the firstradiation beam pulse having such an intensity pattern, each region 1402of the metal layer 52 overlapped by a respective one of the beamlets1400 is melted throughout its entire thickness, while each region 1403of the metal layer 1403 overlapped by a respective one of the shadowregions 1401 remains at least partially unmelted. Each one of the atleast partially unmelted regions 1403 adjoins respective adjacent meltedregions 1402. The metal layer in the at least partially unmelted regions1403 has the relatively small grains with randomly oriented grainboundaries of the metal layer as originally formed.

As shown in FIG. 8B, after irradiation by the first radiation beampulse, melted region 1402 (shown in FIG. 8A) of the metal layer 52 ispermitted to cool and resolidify. During resolidification of each meltedregion 1402, grains grow from each at least partially unmelted region1403 in each adjoining melted region 1402, and in each melted region1402, grains grow from adjoining at least partially unmelted regions1403 in opposite directions towards one another, and abut one anotheralong a respective one of first grain abutment boundaries 1407 locatedapproximately along the center line of each melted region 1402 to formresolidification regions 1404. Each one of the resolidification regions1404 has two columns of horizontally extending (i.e., in the ±Xdirections) grains 1405 and 1406, which abut one another after havinggrown by an abutting grain growth distance, d, of approximately half thewidth of the beamlets. After resolidification of each melted region 1402of the metal layer 52 is completed, the metal layer 52 is irradiated bya second radiation beam pulse having the same intensity pattern as thefirst radiation beam pulse, but where shadow regions and beamletsthereof are shifted with respect to those of the intensity pattern ofthe first radiation beam pulse in the X direction by a distance at leastequal to the width of the shadow region 1401 (shown in FIG. 8A) bymicrotranslation of the sample 40 (shown in FIG. 1A) in the X directionor by microtranslation of the mask 150 (shown in FIG. 1A). In thepresent embodiment the sample 40 is microtranslated in the −X directionby a distance at least equal to the width of the shadow regions 1401,such that the shifted shadow regions 1408 (indicated by dashed lines inFIG. 8B) overlap respective regions having larger grains in each one ofthe solidification regions 1404. Each shifted shadow regions 1408 mayoverlap a region on either side of the first grain abutment boundary1407 in each resolidification region 1404. Advantageously, the shiftedshadow regions 1408 should be relatively close to the first grainabutment boundary 1407 in each resolidification region 1404, but shouldnot overlap the first grain abutment boundary 1407.

Turning now to FIG. 8C, after shifting the intensity pattern, the metallayer 52 (shown in FIG. 1A) is irradiated by the second radiation pulse,which causes each region 1410 (shown in FIG. 8C) of the metal layer 52overlapped by a respective one of the shifted beamlets 1409 to be meltedthroughout its entire thickness, while each region 1411 of the metallayer 52 overlapped by a respective one of the shifted shadow regions1408 remains at least partially unmelted. Each one of the at leastpartially unmelted regions 1411 adjoins respective adjacent meltedregions 1410.

Referring to FIG. 8D, upon cooling and resolidification of the meltedregions 1410, respective grains grow from each at least partiallyunmelted region 1411 in each adjoining melted region 1412. In eachmelted region 1410 respective grains 1412 grow from each adjoining atleast partially unmelted region 1411 in opposite directions towards oneanother, and abut one another along a respective one of second grainabutment boundaries 1413 after the abutting grains having grown by theabutting grain growth distance, d. Each one of the second grain abutmentboundaries 1413 is located approximately along the vertical (i.e., the±Y directions) center line of a respective one of the melted regions1410. Because the at least partially unmelted regions 1411 each containrelatively large grains having lateral grain boundaries extendinggenerally along the horizontal direction (i.e., the ±X directions), thegrains 1412 growing in opposite horizontal directions from each at leastpartially unmelted region 1411 will be seeded by such relatively largegrains contained therein. As shown in FIG. 8D, the resulting grains 1412are wider and longer, and extend between respective adjacent secondgrain abutment boundaries 1413.

As is apparent from the description of the present exemplary embodiment,the width of the melted regions 1402 and 1410 (as determined by thewidth of the beamlets 1400, 1409) after irradiation by the first andsecond radiation beam pulses, respectively, should be no greater thanthat which permits grains growing from the adjoining at least partiallyunmelted regions 1403 and 1411 to respectively reach the first andsecond grain abutment boundaries 1407 and 1413 before nucleation of newgrains occur in the melted regions 1402 and 1410. Typically, each of thefirst and second radiation beam pulses provides a beamlet intensity inthe range of 10 mJ/cm² to 10⁴ mJ/cm² with a pulse duration in the rangeof 10 nsec to 10³ nsec and a pulse repetition rate in the range of 10 Hzto 10³ Hz. It will be understood by those skilled in the art that thesame result may be obtained by shifting the intensity pattern of thesecond radiation beam pulse in the −X direction. Except for the shiftingof the shadow regions and the beamlets, the intensity pattern of thesecond radiation beam pulse is the same as that of the first radiationbeam pulse.

It is noted that interconnect lines for an integrated circuit device maybe advantageously formed from a metal layer having the grain structureshown in FIG. 8D by patterning the segments of the interconnect lines tobe diagonally oriented with respect to the horizontal direction of thegrain boundaries (e.g., oriented at ±45° with respect to the X axis) ofthe LS-processed metal layer in order to minimize electromigration.

Referring to FIGS. 9A and 9B, the above-described LS process may becarried out using a pulsed radiation beam having an intensity pattern,as defined by the mask 150 (shown in FIG. 1A), in which the shadowregions 1901 and beamlets 1902 are oriented diagonally with respect tothe X and Y directions, as shown in FIG. 9A. Then LS processing may becarried out using the same procedure as described above for verticallyoriented (i.e., in the ±Y direction) shadow regions and beamlets, exceptthat the intensity pattern of the second radiation beam pulses isshifted in a direction perpendicular to the diagonally oriented shadowregions 1901 and the beamlets 1902. In this manner, diagonal rows ofrelatively wide and long grains extending between respective adjacentones of diagonally oriented second grain abutment boundaries 1904 areformed.

Referring now to FIGS. 10A–10E, there are illustrated the radiation beampulse intensity pattern and metal layer grain structure at differentstages of LS processing according to a sixth exemplary embodiment of themethod of the present invention. The present exemplary embodiment isadvantageously an extension of the fifth exemplary embodiment describedabove with reference to FIGS. 8A–8D. After completion of the LSprocessing according to the fifth exemplary embodiment to obtain thegrain structure illustrated in FIG. 8D, the sample 40 having the metallayer 52 (shown in FIG. 1A) is rotated by 90° with respect to the secondgrain abutment boundaries 1413 to obtain the grain structure illustratedin FIG. 10A. After the 90° rotation, contiguous columns of relativelylong and wide grains 1412 illustrated in FIG. 8D become contiguous rowsof relatively long and wide grains 1412 depicted in FIG. 10A, and thevertically extending second grain abutment boundaries 1413 in FIG. 8Dbecome horizontally extending second grain abutment boundaries 1413 inFIG. 10A. Each row of grains illustrated in FIG. 10A has a height of λ,which is approximately in the range of 2 μm to 10³ μm.

Referring to FIG. 10A, after the 90° rotation the metal layer 52 of thesample 40 (shown in FIG. 1A) is irradiated by a radiation beam pulsehaving the same intensity pattern as the first radiation beam pulse ofthe fifth exemplary embodiment illustrated in FIG. 8A, having regularlyspaced, relatively wide, linear, stripe-like beamlets 1400 and regularlyspaced, relatively narrow, linear, stripe-like shadow regions 1401, asindicated by dashed lines in FIG. 9A. Irradiation of the metal layer 52of the sample 40 by the first radiation beam pulse after the 90°rotation causes each region 1500 of the metal layer 52 overlapped by arespective one of the beamlets 1400 to melt throughout its entirethickness, while each region 1501 overlapped by a respective one of theshadow regions 1401 remains at least partially unmelted, as illustratedin FIG. 10B. Each at least partially unmelted region 1501 adjoinsadjacent melted regions 1500.

After irradiation by the first radiation beam pulse after the 90°rotation, each melted region of the metal layer 52 is permitted to cooland resolidify. During resolidification of each melted region 1500 ofthe metal layer 52, different single grains grow from each at leastpartially unmelted region 1501 in each adjoining melted region 1500.Referring to FIG. 10C, in each melted region 1500, respective singlegrains grow from adjoining at least partially unmelted regions 1501 inopposite directions towards one another until the grains abut oneanother along a respective one of the third grain abutment boundaries1510 after the abutting grains have grown by a second abutting graingrowth distance, d, of approximately half the width of the beamlets. Thegrain structure of the metal layer 52 after completion ofresolidification following irradiation by the first radiation beam pulseis depicted in FIG. 10C. Because the width of each one of the shadowregions 1401 is sufficient to overlap two grains in each one of the rowsof grains 1412 illustrated in FIG. 10A, the grain structure depicted inFIG. 10C consists of contiguous rows 1502 of large grains separated byhorizontal grain abutment boundaries 1503. In each one of the rows 1502,the grains are separated by respective grain boundaries 1511 andrespective vertical grain abutment boundaries 1510.

After completion of resolidification following irradiation by the firstradiation beam pulse after the 90° rotation, the sample 40 or the mask150 (both shown in FIG. 1A) is microtranslated so as to produce ahorizontal shift of the intensity pattern of a second radiation beampulse in the +X direction, for example. The shifted intensity patternhas shifted beamlets 1504 and shifted shadow regions 1505, as indicatedby dashed lines in FIG. 10C. As shown in FIG. 10D, each region 1506 ofthe metal layer 52 (shown in FIG. 1A) overlapped by a respective one ofthe shifted beamlets 1504 is melted throughout its entire thickness,while each region 1507 overlapped by a respective one of the shiftedshadow regions 1505 remains at least partially unmelted. Each at leastpartially unmelted region adjoins respective adjacent melted regions. Asshown in FIG. 10C, each at least partially unmelted region 1507 containsa single grain in each one of the rows 1502. Therefore, as shown in FIG.10E, when the melted regions 1506 (shown in FIG. 10D) resolidify, arespective single grain in each one of the rows 1502 grows laterallyfrom each at least partially unmelted region 1507 in each adjoiningmelted region 1506, and in each melted region a respective pair ofsingle grains in each one of the rows 1502 grow from adjoining at leastpartially unmelted regions in opposite directions towards one another,and abut one another along a respective one of fourth vertical grainabutment boundaries 1512 after the abutting grains have grown by thecharacteristic growth distance, d. When resolidification afterirradiation by the second radiation beam pulse following the 90°rotation is completed, the grain structure of the metal layer 52 isillustrated in FIG. 10E. As shown in FIG. 10E, the resulting grainstructure consists of rows 1508 of generally square single grain regionshaving dimensions λ×λ, each single grain region being bounded byrespective ones of the horizontal grain abutment boundaries 1503 andrespective ones of the second vertical grain abutment boundaries 1512,where λ is the distance between adjacent ones of the second grainabutment boundaries 1413 shown in FIG. 10A. The typical radiation beampulse intensity, pulse duration and pulse repetition interval are thesame as for the fifth exemplary embodiment.

Turning now to FIGS. 11A–11D, there are illustrated the radiation beampulse intensity pattern and the metal layer grain structure at differentstages of LS processing according to a seventh exemplary embodiment ofthe method of the present invention. Referring to FIG. 11A, a sample 40has disposed thereon a metal layer 52 which has been prepatterned into arelatively narrow strip having a width, for example, in the range of 0.1μm to 10 μm. The metal layer strip 52, which is formed of copper, forexample, and which has a predefined contour conforming to the Manhattangeometry, is irradiated by a first radiation beam pulse having anintensity pattern that includes a plurality of relatively narrow,linear, stripe-like shadow regions 1600 positioned to overlap the metallayer strip 52 at regularly spaced intervals along the predefinedcontour. The intensity pattern of the first radiation beam pulse alsoincludes a beamlet that overlaps all regions of the metal layer strip 52that are not overlapped by a respective one of the shadow regions 1600.The shadow regions 1600 advantageously have a width in the range of lessthan 1 μm to 10 μm and a length in the range of 2 μm to 100 μmsufficient to completely overlap the width of the metal layer strip 52after the intensity pattern of the radiation beam pulse has beenshifted, as described hereinbelow.

When the metal layer strip 52 is irradiated by the first radiation beampulse, each region of the metal layer strip overlapped by the beamlet ismelted throughout its entire thickness, while each region of the metallayer strip overlapped by a respective one of the shadow regions 1600remains at least partially unmelted. Each at least partially unmeltedregion adjoins respective adjacent melted regions, and contains smallgrains with randomly oriented grain boundaries of the metal layer strip52 as originally formed. After irradiation by the first radiation beampulse, each melted region is permitted to cool and resolidify. Referringto FIG. 11B, during resolidification of each melted region, grains 1601grow laterally from each one of the at least partially unmelted regionsin adjoining melted regions. Here, because of the narrowness of themetal layer strip 52, only single grains 1601 can grow in the metallayer strip 52. Therefore, single grains 1601 grow from each one of theat least partially unmelted regions 1602 of the metal layer strip 52 ineach adjoining melted region, and in each melted region respectivegrains 1601 grow from adjoining melted regions in opposite directionstowards one another, and abut one another at a respective one of aplurality of first grain abutment boundaries 1603.

The grain structure of the metal layer strip 52 after completion ofresolidification following irradiation by the first radiation beam pulseis represented in FIG. 11B. As shown in FIG. 11B, the grain structure ofeach at least partially unmelted region 1602 of the metal layer strip 52has clusters of small grains with randomly oriented grain boundaries,while the grain structure of each resolidified region has relativelylong grains 1601 grown from adjoining at least partially unmeltedregions 1602 in opposite directions towards one another so as to abut ata respective one of a plurality of first grain abutment boundaries 1603after the abutting grains have grown by an abutting grain growthdistance of approximately half the distance between adjacent shadowregions 1600 along the contour of the metal strip 52.

Turning now to FIG. 1C, after completion of resolidification followingirradiation by the first radiation beam pulse, the metal layer strip 52is irradiated by a second radiation beam pulse having the same intensitypattern as the first radiation beam pulse, but where the shadow regions1604 thereof are shifted with respect to those of the intensity patternof the first radiation beam pulse so that each shifted shadow regionoverlaps a respective one of the single grain regions 1601 of the metallayer strip 52. While the beamlet of the intensity pattern of the secondradiation beam pulse is also shifted, it still overlaps all regions ofthe metal layer strip 52 not overlapped by a respective one of theshifted shadow regions 1604. In the present exemplary embodiment, theshifting of the shadow regions 1604 and the beamlet with respect to themetal layer strip 52 is achieved by microtranslating the sample 40(shown in FIG. 1A) in a diagonal direction (e.g., in the A directionoriented at 45° relative to the X axis) with respect to the segments ofthe metal layer strip 52. In the alternative, the shifting of the shadowregions 1604 may also be achieved by microtranslating the mask 150(shown in FIG. 1A) instead of microtranslating the sample 40.

When the metal layer strip 52 is irradiated by the second radiation beampulse, each region of the metal layer strip 52 overlapped by the shiftedbeamlet is melted throughout its entire thickness, while each region ofthe metal layer strip overlapped by a respective one of the shadowregions 1604 remains at least partially unmelted. Each at leastpartially unmelted region adjoins respective adjacent melted regions andcontains a respective single grain. After irradiation by the secondradiation beam pulse, each melted region of the metal layer strip 52 ispermitted to cool and resolidify. During resolidification, therespective single grain in each at least partially unmelted region growsin each adjoining melted region, and in each melted region respectivesingle grains grow from adjoining at least partially unmelted regions inopposite directions towards one another and abut one another at arespective one of second grain boundaries 1606 after the abutting grainshave grown by the abutting grain growth distance.

The grain structure of the metal layer strip 52 after completion ofresolidification following the second radiation beam pulse isillustrated in FIG. 11D. The grain structure consists of single grainregions 1605 abutting at respective second grain abutment boundaries1606, the second grain abutment boundaries 1606 being substantiallyperpendicular to the metal layer strip 52 at respective locations of theboundaries 1606. Advantageously, in the foregoing exemplary embodiment,the radiation beam pulses provide a beamlet intensity in the range of 10mJ/cm² to 10⁴ mJ/cm2 with a pulse duration in the range of 10 nsec to10³ nsec and a pulse repetition rate in the range of 10 Hz to 10³ Hz.Except for the shifting of the shadow regions and the beamlets of theintensity pattern of the second radiation beam pulse with respect tothose of the intensity pattern of the first radiation beam pulse, theintensity patterns of the first and second radiation beam pulses are thesame.

Referring to FIGS. 12A–12D, there are illustrated the radiation beampulse intensity pattern and the metal layer grain structure at differentstages of LS processing according to an eighth exemplary embodiment ofthe method of the present invention. In FIG. 12A there is shown aportion of the substrate 40 having a metal layer 52 which is formed ofcopper, for example, and which has been patterned into a strip having aright angle bend. Advantageously, the metal layer strip 52 has a widthof 10 μm or narrower and is representative of metal layer interconnectlines of modern integrated circuit devices, in which the metalinterconnect lines are laid out to have the Manhattan geometry.

The metal layer strip 52 is irradiated by a first radiation beam pulsehaving an intensity pattern, as defined by the mask 150 (shown in FIG.1A), that includes a plurality of regularly spaced-apart, relativelywide, linear, stripe-like beamlets 1700 and a plurality of regularlyspaced-apart, relatively narrow, linear, stripe-like shadow regions 1701with both the shadow regions 1701 and the beamlets 1700 extending alongthe Y direction. Each one of the beamlets 1700 is positioned in betweenand adjoining respective adjacent shadow regions 1701. Each right anglesegment of the metal layer strip 52 is oriented diagonally with respectto the shadow regions 1701 and beamlets 1700. Preferably, each rightangle segment of the metal layer strip 52 is oriented either in the Adirection (i.e., at 45° with respect to the X axis) or in the Bdirection (i.e., at −45° with respect to X axis). Advantageously, thewidth of the beamlets 1700 is in the range of less than 1 μm to 100 μm,and the width of the shadow regions 1701 is in the range of less than 1μm to 10 μm. Upon irradiation by the first radiation beam pulse, eachregion 1703 of the metal layer strip 52 overlapped by respective ones ofthe beamlets 1700 is melted throughout its entire thickness, while eachregion of the metal layer strip 52 overlapped by a respective one of theshadow regions 1701 remains at least partially unmelted. Each at leastpartially unmelted region adjoins respective adjacent melted regions,and contains small grains with randomly oriented grain boundaries of themetal layer strip 52 as it was originally formed.

Following irradiation by the first radiation beam pulse, each meltedregion 1703 of the metal layer strip 52 is permitted cool andresolidify. During such resolidification, single grains grow from eachat least partially unmelted region of the metal layer strip 52 in eachadjoining melted region 1703, and in each melted region respectivesingle grains grow from adjoining at least partially unmelted regions inopposite directions towards one another, and abut one another at arespective one of a plurality of first grain abutment boundaries 1706after the abutting grains have grown by an abutting grain growthdistance of approximately half the distance between adjacent shadowregions 1701 along the contour of the metal strip 52. Because of thenarrowness of the metal layer strip 52, only single grains can grow inthe strip.

The grain structure of the metal layer strip 52 after completion ofresolidification following irradiation by the first radiation beam pulseis illustrated in FIG. 12B. Referring to FIG. 12B, the grain structurecomprises clusters of small grains having randomly oriented grainboundaries in each at least partially unmelted region 1704, single grainregions 1705 grown in melted regions 1703 adjoining respective at feastpartially unmelted regions 1704, and first grain abutment boundaries1706 where respective single grains 1705 growing in opposite directionsin the melted regions 1703 abut one another.

Turning now to FIG. 12C, after completion of resolidification followingirradiation by the first radiation beam pulse, the metal layer strip 52is irradiated by a second radiation beam pulse having the same intensitypattern as the first radiation beam pulse, but where the beamlets 1707and the shadow regions 1708 are shifted with respect to those of theintensity pattern of the first radiation beam pulse in a directionperpendicular to the beamlets and shadow regions by a distance at leastequal to the width of the shadow regions 1701 and 1708 but less than thedistance that would cause the shadow regions 1708 to overlap the firstgrain abutment boundary 1706. In this manner, each shifted shadow region1708 overlaps a respective one of the single grain regions 1705 (shownin FIG. 12B). In the present exemplary embodiment, shifting of theintensity pattern is in the +X direction, and is obtained bymicrotranslating the sample 40 in the −X direction. Alternatively, theintensity pattern (i.e., the beamlets 1707 and the shadow regions 1708)may be shifted in the −X direction by translating the sample 40 in the+X direction. As a further alternative, the mask 150 (shown in FIG. 1A)may be microtranslated instead of the sample to shift the intensitypattern of the second radiation beam pulse in either the X direction orthe −X direction.

Upon irradiation by the second radiation beam pulse, each region of themetal layer strip 52 overlapped by a respective one of the shiftedbeamlets 1707 is melted throughout its entire thickness, while eachregion of the metal layer strip 52 overlapped by a respective one of theshadow regions 1708 remains at least partially unmelted. Each at leastpartially unmelted region adjoins respective adjacent melted regions andcontains a respective single grain region. After irradiation by thesecond radiation beam pulse, each melted region of the metal layer strip52 is permitted to cool and resolidify. During resolidification of eachmelted region 1709, the respective single grain in each at leastpartially unmelted region grows in each adjoining melted region 1709,and in each melted region, respective single grains grow from adjoiningat least partially unmelted regions in opposite directions towards oneanother, and abut one another at a respective one of a plurality ofsecond grain abutment boundaries 1711, as shown in FIG. 12D.

The grain structure of the metal layer strip 52 after completion ofresolidification following the second radiation beam pulse is depictedin FIG. 12D. The grain structure shown comprises single grain regions1710 that extend between respective adjacent second grain abutmentboundaries 1711, each second grain abutment boundary 1711 beingdiagonally oriented at approximately 45° with respect to the metal layerstrip 52 at the location of the boundary 1711. Advantageously, in theforegoing exemplary embodiment, each radiation beam pulse provides abeamlet intensity in the range of 10 mJ/cm² to 10⁴ mJ/cm² with a pulseduration in the range of 10 nsec to 10³ nsec and a pulse repetition ratein the range of 10 Hz to 10³ Hz.

The exemplary embodiment illustrated in FIGS. 12A–12D may be applied toa multiplicity of prepatterned metal layer strips having the Manhattangeometry, such as the interconnect lines of a partially fabricatedintegrated circuit device, of multiple partially fabricated integratedcircuit devices or of all partially fabricated integrated circuitdevices on an entire wafer, at the same time.

Referring to FIGS. 13A–13C, there are illustrated the radiation beampulse intensity pattern and metal layer grain structure at differentstages of LS processing according to a ninth exemplary embodiment of themethod of the present invention. In the present exemplary embodiment, ametal layer strip, which is formed of copper, for example, having singlegrain sections and grain boundaries forming large angles with respect tothe direction of the metal layer strip, is formed by irradiating a metallayer 52 on a sample 40 (both shown in FIG. 1A) with a radiation beampulse having an intensity pattern that includes a beamlet that conformsto the same contour as the metal layer strip to be formed, but which iswider than the metal layer strip. As shown in FIG. 13A, a portion of ametal layer 52 is irradiated by a radiation beam pulse having anintensity pattern that includes a stripe-like beamlet 1800 having aright angle bend and a shadow region that overlaps all regions of themetal layer not overlapped by the beamlet 1800. A region 1801 of themetal layer 52 overlapped by the beamlet 1800 is melted throughout itsentire thickness, while each region overlapped by the shadow regionremains at least partially unmelted. The melted region 1801 adjoinsadjacent at least partially unmelted regions along its two edges 1802and 1803. Advantageously, the width of the beamlet 1800 is in the rangeof 1 μm to 10 μm for forming a metal layer strip having a width in therange of 0.1 μm to 10 μm.

Following irradiation by the radiation beam pulse, the melted region1801 of the metal layer 52 is permitted to cool and resolidify. Duringresolidification of the melted region 1801, grains grow laterally in themelted region 1801 from its two at least partially unmelted edges 1802and 1803. As illustrated in FIG. 13B, two rows of grains 1805 and 1806growing laterally towards one another from the opposing edges 1802 and1803, respectively, abut one another along a grain abutment boundary1807 that approximately coincides with the center line of the meltedregion 1801 so as to form a resolidification region 1804.

After the melted region 1801 of the metal layer 52 has fullyresolidified, the grain structure of the resulting resolidificationregion 1804 as illustrated in FIG. 13B, has two rows of grains 1805 and1806 which abut along the grain abutment boundary 1807. A relativelynarrow metal layer strip is formed by patterning the metal layer 52having resolidification region 1804. In the present exemplaryembodiment, a strip like region 1807 (indicated by dashed lines in FIG.13B) in the lower row of grains 1806 close to but not overlapping thegrain abutment boundary 1807 is formed by conventional photolithographyand etching of the metal layer 52.

The metal layer strip 1809 obtained after patterning of the metal layer52 is shown in FIG. 13C. As shown in FIG. 13C, the metal layer strip1809 consists of single grain sections 1810 separated from one anotherby grain boundaries 1811 which generally form large angles (i.e., closeto 90°) with respect to the metal layer strip 1809 at respectivelocations of the grain boundaries 1811. In the foregoing exemplaryembodiment, the radiation beam pulse provides a beamlet intensity in therange of 10 mJ/cm² to 10⁴ mJ/cm² with a pulse duration in the range of10 nsec to 10³ nsec.

While the present exemplary embodiment forms the metal layer strip 1809from a strip-like region 1808 in the lower row of grains 1806, it isnoted that a similar metal layer strip may be formed from a strip-likeregion in the other row of grains 1805. It is also noted that while thewidth of the beamlet in the exemplary embodiment is sufficiently narrowso that the two rows of grains 1805 and 1806 of the resolidificationregion 1804 abut at the grain abutment boundary 1807, a wider beamlet1800 may be used to melt a wider region 1801 of the metal layer 52 sothat growth of the rows of grains 1805 and 1806 do not abut one anotherbefore the melted region is completely resolidified. In suchcircumstances the two rows of grains 1805 and 1806 are separated by afine grain metal layer region formed by nucleation (not shown) extendingalong the central portion of the resolidification region, and the metallayer strip 1809 may be formed from strip-like regions in either one ofthe two non-abutting rows of grains 1805 and 1806. The characteristicgrowth distance of each of the two non-abutting rows of grains 1805 and1806 depends primarily on the thermal evolution of the melted metalregion 1801. Advantageously, the strip-like region from which the metallayer strip 1809 is formed lies close to but does not overlap the finegrain region (not shown) separating the two rows of grain 1805 and 1806.

Referring to FIGS. 14 and 15A–15G, there are illustrated the irradiationpaths, the radiation beam pulse intensity pattern and metal layer grainstructure at different stages of LS processing according to a tenthexemplary embodiment of the method of the present invention. Turningfirst to FIG. 14, there is shown a sample 40 having a metal layer 52formed of copper, for example, disposed thereon. Referring back to theapparatus illustrated in FIG. 1A, the sample 40 is placed on the sampletranslation stage 180, which is controlled by the computer 106. A fixedposition pulsed radiation beam 164 having an intensity pattern definedby the mask 150 impinges the metal layer 52 on the sample 40. Bycontrolling the motion of the sample translation stage 180 in the X andY directions, the computer 106 controls the relative position of thesample 40 with respect to the stationary pulsed radiation beam 164 whichirradiates the metal layer 52 on the sample 40. The pulse duration, thepulse repetition rate and the energy of each pulse of the pulsedradiation beam 164 are also controlled by the computer 106.

In the present embodiment the sample 40 (shown in FIG. 1A) is translatedwith respect to the stationary pulsed radiation beam 164 (shown in FIG.1A) in order to sequentially irradiate successive portions of the metallayer 52 (shown in FIG. 1A) along predefined paths of irradiation toobtain lateral growth of large grains having controlled grain size andshape, and controlled grain boundary location and orientation in themetal layer 52. The pulses of the pulsed radiation beam 164 are notlimited to any particular intensity pattern, so long as each beamlet ofthe intensity pattern of each radiation beam pulsed has sufficientenergy to melt a region of the metal layer 52 overlapped by the beamletthroughout its entire thickness, and each melted region of the metallayer 52 has sufficiently small dimensions to allow lateral growth ofgrains in the melted region.

For simplicity of illustration the paths of irradiation are shown inFIG. 14 in the frame of reference of the translating sample 40 so thatthe stationary pulsed radiation beam 164 is depicted as traversing astationary sample.

Turning back to FIG. 14, in the exemplary embodiment the metal layer 52on the sample 40 is subdivided for processing purposes into a number ofcolumns extending in the Y direction (e.g., a first column 205, a secondcolumn 206, etc.). The positions and dimensions of the columns of thesubdivided metal layer 52 are stored in the computer 106 (shown in FIG.1A) and utilized by the computer to control the processing of the metallayer 52 on the sample 40. Exemplary dimensions of each column may be 2cm in the X direction by 40 cm in the Y direction so as to subdivide themetal layer 52 on the sample 40 into, for example, 15 columns. It ispreferable to have the irradiation of adjacent columns overlap oneanother by a small area so as to avoid the possibility of having anyunirradiated areas of the metal layer 52. The overlapping area may havea width of 50 μm, for example.

Referring again to FIG. 1A, the computer 106 causes the pulsed radiationbeam 164 to be emitted and the sample 40 to be positioned so that thepulsed radiation beam 164 impinges on a first location 220 in the frameof reference of the sample 40. The sample 40 is then accelerated in the+Y direction under the control of the computer 106 to reach apredetermined velocity with respect to the stationary pulsed radiationbeam 164, which traces a first path 225 not on the sample 40. It isnoted again that the path 225 is not the result of movement of thepulsed radiation beam 164, which is stationary, but represents themovement of the sample 40 towards the stationary pulsed radiation beam.

When the upper edge 210 of the sample 40 reaches the position ofimpingement of the pulsed radiation beam 164, the sample is moving atthe predetermined velocity with respect to the stationary pulsedradiation beam 164. Thereafter, the sample 40 is translated in the +Ydirection at the predetermined velocity so that the pulsed radiationbeam 164 irradiates successive portions of the metal layer 52 on thesample 40 at a predetermined pulsed repetition rate along a secondirradiation path 230, which traverses the length of the sample 40 in theY direction. When the lower edge 211 of the sample 40 reaches the fixedposition of impingement of the pulsed radiation beam 164, translation ofthe sample 40 is slowed along a third path 235 until coming to a fullstop when the fixed position of impingement of the pulsed radiation beam164 is at a second location 240 with respect to the sample 40. In thepresent embodiment the predetermined pulse repetition rate is, forexample, in the range of 50 Hz to 10³ Hz pulses/sec and each pulseprovides a beamlet intensity in the range of 10 mJ/cm² to 10⁴ mJ/cm²with a pulse duration in the range of 10 nsec to 10³ nsec.

Exemplary grain structures of the metal layer 52 during continuoussequential irradiation thereof by radiation beam pulses having anexemplary intensity pattern while the pulsed radiation beam 164 istraversing the irradiation paths 230 are illustrated in FIGS. 15A–15D.Referring to FIG. 15A, in the present exemplary embodiment the intensitypattern 300 of the pulsed radiation beam 164 has a square shape withregularly spaced-apart, relatively-narrow, linear, stripe-like shadowregions 301 and regularly spaced-apart, relatively wide, linear,stripe-like beamlets 302, each beamlet being positioned in between andadjoining respective adjacent shadow regions. Both the shadow regions301 and the beamlets 302 extend along the Y direction. The dimensions ofthe intensity pattern 300 are 0.1 cm by 1.5 cm. The dimensions of eachshadow region 301 are 2 μm by 1 cm, and the dimensions of each beamlet302 are 4 μm by 1 cm. When a portion of the metal layer 52 immediatelyafter the upper edge 210 of the sample 40 is irradiated by a firstradiation beam pulse, each region 303 of the irradiated portion of themetal layer 52 overlapped by a respective one of the beamlets 302 of theintensity pattern of the first radiation pulse is melted throughout itsentire thickness, while each region 323 of the irradiated portionoverlapped by a respective one of the shadow regions 301 of theintensity pattern of the first radiation beam pulse remains at leastpartially unmelted.

Turning now to FIG. 15B, before irradiation by a second radiation beampulse, in accordance with the predetermined pulse repetition rate, eachregion 303 of the metal layer 52 melted by the first radiation beampulse resolidifies to form two columns of grains 304 and 305 growntowards one another from adjoining at least partially unmelted regions323 (shown in FIG. 15A) and abutting one another along a respective oneof a plurality of grain abutment boundaries 306 after the abuttinggrains have grown by an abutting grain growth distance of approximately2 μm. Both columns of grains 304 and 305 in each one of theresolidification regions 307 have a respective central portion in whichgrain boundaries form large angles (i.e., close to 90°) with respect tothe irradiation path 230. As shown in FIG. 15B, while resolidificationof the melted regions 303 is taking place, the sample is beingtranslated with respect to the stationary pulsed radiation beam 164along the irradiation path 230 so that when the metal layer 52 isirradiated by the second radiation beam pulse, its intensity pattern308, indicated by dashed lines in FIG. 15B, has translated so as to onlypartially overlap the resolidification regions 307.

As shown in FIG. 15C, regions 309 of the metal layer 52 overlapped byrespective ones of the beamlets 305 of the intensity pattern 308 of thesecond radiation beam pulse are each melted throughout its entirethickness, while each region 326 of the metal layer 52 overlapped by arespective one of the shadow regions 324 of the intensity pattern 308 ofthe second radiation beam pulse remains at least partially unmelted. Inaddition, portions of the resolidification regions 307 that are notoverlapped by the beamlets 325 of the intensity pattern 308 of thesecond radiation beam pulse also remain at least partially unmelted. Asillustrated in FIG. 15D, during resolidification of the melted regions309 between successive radiation beam pulses, the columns of grains 311and 312 in each resolidification region 310 increase in length and haverespective central portions in which the grain boundaries form largeangles (i.e., close to 90°) with respect to the irradiation path 230.Because continuous translation of the sample 40 with respect to thestationary pulsed radiation beam 164 takes place between successiveradiation beam pulses, during which the melted regions 309 resolidify,when the metal layer 52 is irradiated by a third radiation beam pulse,the intensity pattern 313 thereof (as indicated by dashed lines in FIG.15D) is translated with respect to the resolidification regions 310 sothat the beamlets 328 of the intensity pattern 313 of the thirdradiation beam pulse only partially overlap the resolidification regions310. In this manner, continuous translation of the sample along theirradiation path 230 in a first pass of column 205 at the predeterminedvelocity together with irradiation by successive radiation beam pulsesat the predetermined pulse repetition rate results in the formation ofresolidification regions extending along the entire length of the secondirradiation path 230, each one of the resolidfication regions having twoabutting columns of grains with respective portions central to theresolidification region in which grain boundaries form large angles withrespect to the irradiation path 230.

Turning back to FIG. 14, after the stationary pulsed radiation beam 164in the frame of reference of the translating sample 40 has come to astop at location 240, the sample 40 is microtranslated in the Xdirection under the control of the computer 106 so that the pulsedradiation beam traces a fourth path 245 until the beam impinges location247. The sample 40 is then accelerated in the −Y direction so that thepulsed radiation beam traverses a fifth path 250 until the sample 40reaches the predetermined velocity of translation by the time the loweredge 211 of the sample 40 reaches the position of impingement of thebeam. Thereafter, the sample 40 is translated at the predeterminedvelocity in the −Y direction for the entire length of a sixthirradiation path 255, while the pulsed radiation beam sequentiallyirradiates the metal layer 52 on the sample 40 at the predeterminedpulsed repetition rate.

Referring to FIG. 15E, there is shown a portion 317 of the metal layerin column 205 immediately above the lower edge 211 of the sample 40after microtranslation along path 245 and traversal of path 250. Theportion 317 of the metal layer 52 in column 205, which is shown aftercompletion of traversal of the irradiation path 230 in the first pass bythe pulsed radiation beam, has a multiplicity of resolidificationregions 316 each having two abutting columns of grains 314 and 315,which extend along the entire length of the column 205. Eachresolidification region 316 is bounded on its two sides by twounirradiated regions 318, which also extend along the entire length ofthe column 205. The intensity pattern 319 of the first radiation beampulse of the second pass to irradiate the metal layer 52 in column 205after the microtranslation is indicated by dashed lines in FIG. 15E. Theshifted intensity pattern 319 has a multiplicity of shadow regions 329that partially overlap the two columns of grains 314 and 315 in thecentral portion of respective ones of the resolidification regions 316,and beamlets 330 that overlap respective ones of the unirradiatedregions 318 and overlap a portion of the columns of grains 314 and 315at the edges of respective adjacent resolidification regions 316. Whenthe portion 317 of the metal layer 52 is irradiated by a first radiationbeam pulse having the intensity pattern 319, regions 320 of the metallayer overlapped by respective ones of the beamlets 330 are each meltedthroughout their entire thickness, while regions 323 of the metal layeroverlapped by respective ones of the shadow regions 329 remain at leastpartially unmelted, as shown in FIG. 15F. Each at least partiallyunmelted region 323 adjoins respective adjacent melted regions 320.After irradiation by the first radiation beam pulse, the melted regions320 are permitted to cool and resolidify. During resolidification of themelted regions 320, the at least partially unmelted portions 321 and 322of the columns of grains 314 and 315 central to each one of theresolidification regions 316 seed lateral growth of grains in respectiveadjoining melted regions 320. As shown in FIG. 15G, whenresolidification of the melted regions 320 is completed, there is formeda resolidification region 333 having contiguous columns 332 ofrelatively long grains having grain boundaries oriented generally alongthe X direction.

While resolidification of the melted regions 320 is taking place,continuous translation of the sample 40 with respect to the pulsedradiation beam 164 (shown in FIG. 1A) causes the intensity pattern 331of the next radiation beam pulse (indicated in FIG. 15G by dashed lines)to be translated with respect to the resolidification region 333 so asto partially overlap the resolidification region 333. In this manner,continuous translation of the sample so that the pulsed radiation beam164 traverses the irradiation path 255 at the predetermined velocity,together with irradiation of the first column 205 the metal layer 52with radiation beam pulses at the predetermined pulsed repetition ratein the second pass will result in contiguous columns of relatively longgrains 332 having grain boundaries oriented generally in the X directionto be formed along the entire length of the first column 205.

After the pulsed radiation beam 164 has traversed the sixth irradiationpath 255 in the manner described above, continuous LS processing of thefirst column 205 is completed. Referring again to FIG. 14, when thesample 40 is translated under the control of the computer 106 (shown inFIG. 1A) so that the pulsed radiation beam 164 impinges the upper edge210 of the sample 40, the velocity of the sample 40 is again slowed withrespect to the pulsed radiation beam 164 while the beam traverses aseventh irradiation path 260 so that the sample 40 comes to a completestop by the time the pulsed radiation beam 164 impinges upon a location265 in the frame of reference of the sample 40. The sample 40 is thentranslated to the next column 206 so that the pulsed radiation beam 164impinges a fifth location 272 after traversing an eighth path 270 in theframe of reference of the sample 40. Thereafter, the sample 40, underthe control of the computer 106, is held stationary for a predeterminedperiod of time to allow any vibrations caused by the relatively longtranslation of the sample 40 from one column to another to settle. Inparticular, for the sample 40 to be positioned so that the pulsedradiation beam 164 can impinge along irradiation paths in the secondcolumn 206, the sample is translated by 2 cm in the X direction forcolumns having a width of 2 cm in the X direction. The continuous LSprocedure described above for the first column 205 is then repeated forthe second column 206 and thereafter for each of the remaining columnsof the sample 40. In this manner, all the columns of the sample 40 maybe continuous LS processed with only minimal total settling time beingrequired.

Delays to allow vibrations of the sample 40 to settle are required onlywhen continuous LS processing has been completed for an entire column(e.g., the first column 205) of the sample 40, and the sample 40 istranslated so that the pulsed radiation beam is in position to scan anirradiation path in the next column (e.g., the second column 206) of thesample 40 in a first pass. Using the exemplary dimensions of the sample40 (e.g., 30 cm×40 cm), there are only fifteen columns to be continuousLS processed in such an exemplary sample. Accordingly, the number of“translate and settle” delays that will be encountered during continuousLS processing of such an exemplary sample is either 14 or 15, dependingupon whether a settling delay is required when the sample 40 ispositioned for continuous LS processing of the first column.

In accordance with the present invention, LS processing of a large metallayer 52 may be carried out by subdividing the metal layer 52, forprocessing purposes, into contiguous sections, and carrying out LSprocessing in each of the sections one at a time, as illustrated inFIGS. 16A–16E. As shown in FIG. 16A, the sample 40 is initiallypositioned for LS processing in a first section 410 of the metal layer52. It is noted that the first section 410 borders the left edge of themetal layer 52. After LS processing in accordance with the presentinvention is completed in section 410, as indicated by the crossed linesin the block representing the first section 410, the sample 40 istranslated in the −X direction so as to be positioned for LS processingof the next contiguous section 420.

Referring to FIG. 16B, after completion of LS processing of section 420,as indicated by the crossed lines in the block representing thatsection, the sample is again translated in the −X direction so as to bepositioned for LS processing of the next contiguous section 430.Advantageously, in carrying out LS processing in a given section, theradiation beam pulses that irradiate the section overlap the previouslyprocessed contiguous section by a small amount (e.g., 50 μm), asindicated by the thick line representing the common border betweencontiguous LS processed sections. As shown in FIG. 16C, the procedure ofcompleting LS processing in accordance with the present invention in asection of the metal layer 52 and translation of the sample 40 in the −Xdirection so as to position the sample for LS processing of the nextcontiguous section is repeated until the sample 40 is positioned for LSprocessing in accordance with the present invention of a section 450that borders the right edge of the metal layer 52.

Turning to FIG. 16D, after completion of LS processing in accordancewith the present invention in section 450, the sample 40 is translatedin the −Y direction until it is positioned for LS processing of the nextcontiguous section 460. Referring to FIG. 16E, after completion of LSprocessing in accordance with the present invention in section 460 thesample 40 is translated in the +X direction until it is positioned forLS processing of the next contiguous section 470. Thereafter, the stepsof completing LS processing in a section and translating the sample inthe +X direction until the sample is in position for LS processing ofthe next contiguous section are repeated until the sample 40 ispositioned for LS processing of section 490, which borders on the leftedge of the metal layer 52. As shown in FIG. 16G, after completion of LSprocessing in accordance with the present invention in section 490, thesample 40 is translated in the +Y direction until it is positioned forLS processing of the next contiguous section 500. Thereafter, the stepsof completing LS processing in accordance with the present invention ina section and translating the sample in the −X direction until it ispositioned for LS processing of the next contiguous section are repeateduntil the sample 40 is positioned for LS processing of a section (notshown) that borders a right edge of the metal layer 52. The foregoingillustrative procedure is carried out until all sections of the metallayer 52 are LS-processed in accordance with the present invention, forexample in accordance with the third, fourth or fifth exemplaryembodiments described above. It is noted that various alternativeschemes will be apparent to those skilled in the art for traversing thesections of the metal layer by successive translations from one sectionto another, such as by traversing the sections by columns instead of byrows.

Alternatively, instead of completing LS processing in accordance withthe present invention in one section of the metal layer 52 beforetranslating the sample 40 for LS processing of a next contiguoussection, the processing steps may be carried out one step at a time ineach section one section at a time. Since LS processing in accordancewith the present invention, as exemplified by the third, fourth or fifthillustrative embodiments described above, each require irradiating themetal layer 52 with a first radiation beam pulse having a predeterminedintensity pattern, permitting the regions melted by the first radiationbeam pulse to resolidify, irradiating the metal layer with a secondradiation beam pulse having a shifted intensity pattern, and so forthuntil the desired grain size, grain shape, and grain boundary locationand orientation are obtained, LS processing of a metal layer on asection-by-section basis may be carried out by irradiating each sectionof the metal layer 52 by the first radiation beam pulse using theillustrative sample translation scheme depicted by FIGS. 16A–16G. Whenall sections of the metal layer 52 have been irradiated by the firstradiation beam pulse, the sample 40 is translated so that it is inposition for irradiation on a section-by-section basis by a secondradiation beam pulse having an intensity pattern shifted with respect tothat of the first radiation beam pulse by a desired distance and in adesired direction after the regions melted by the first radiation beampulse in each section to be irradiated by the second radiation beampulse has completely solidified. In this manner, the sections of themetal layer 52 may undergo further irradiations by radiation beam pulseshaving shifted intensity patterns and resolidification after irradiationby each radiation beam pulse on a section-by-section basis until adesired grain size, grain shape, and grain boundary location andorientation in the metal layer 52 is obtained.

The foregoing exemplary embodiments merely illustrate the principles ofthe present invention. Various modifications and alterations to thedescribed embodiments will be apparent to those skilled in the art inview of the teachings herein without departing from the scope of theinvention, as defined by the appended claims.

1. A method for processing a thin metal layer disposed on a substratecomprising the steps of: (a) irradiating at least a portion of the metallayer with a first radiation beam pulse having an intensity pattern thatincludes at least one beamlet and at least one shadow region, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one beamlet being melted throughout itsentire thickness, each region of the at least a portion of the metallayer overlapped by a respective one of the at least one shadow regionremaining at least partially unmelted, each at least partially unmeltedregion adjoining at least one adjacent melted region, wherein theintensity pattern of each radiation beam pulse is defined by a maskthrough which the radiation beam pulse passes; (b) permitting eachmelted region of the at least a portion of the metal layer irradiated bythe first radiation beam pulse to resolidify, wherein duringresolidification of each melted region, grains grow therein from eachone of the at least one adjoining at least partially unmelted region;(c) irradiating at least a portion of the metal layer with a furtherradiation beam pulse having the same intensity pattern as the previousradiation beam pulse, wherein the previous radiation beam pulse is thefirst radiation beam pulse of step (a), but where the at least onebeamlet and the at least one shadow region thereof are shifted withrespect to the at least a portion of the metal layer, each region of theat least a portion of the metal layer overlapped by a respective one ofthe at least one shifted beamlet being melted throughout its entirethickness, each region of the at least a portion of the metal layeroverlapped by a respective one of the at least one shifted shadow regionremaining at least partially unmelted, each at least partially unmeltedregion adjoining at least one melted region, wherein the intensitypattern of the further radiation beam pulse is shifted with respect tothe at least a portion of the metal layer by shifting the substratehaving the metal layer; (d) permitting each melted region of the atleast a portion of the metal layer irradiated by the further radiationbeam pulse to resolidify, wherein during resolidification of each meltedregion, grains grow therein from each one of the at least one adjoiningat least partially unmelted region, the further radiation beam pulsebeing the previous radiation beam pulse for further processing; and (e)repeating steps (c) and (d) in combination, if needed, with the furtherradiation beam pulse in each step becoming the previous radiation beampulse in the next step, until a desired grain structure is obtained inthe at least a portion of the metal layer.
 2. A method for processing athin metal layer disposed on a substrate comprising the steps of: (a)irradiating at least a portion of the metal layer with a first radiationbeam pulse having an intensity pattern that includes at least onebeamlet and at least one shadow region, each region of the at least aportion of the metal layer overlapped by a respective one of the atleast one beamlet being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one shadow region remaining at leastpartially unmelted, each at least partially unmelted region adjoining atleast one adjacent melted region, wherein the intensity pattern of eachradiation beam pulse is defined by a mask through which the radiationbeam pulse passes; (b) permitting each melted region of the at least aportion of the metal layer irradiated by the first radiation beam pulseto resolidify, wherein during resolidification of each melted region,grains grow therein from each one of the at least one adjoining at leastpartially unmelted region; (c) irradiating at least a portion of themetal layer with a further radiation beam pulse having the sameintensity pattern as the previous radiation beam pulse, wherein theprevious radiation beam pulse is the first radiation beam pulse of step(a), but where the at least one beamlet and the at least one shadowregion thereof are shifted with respect to the at least a portion of themetal layer, each region of the at least a portion of the metal layeroverlapped by a respective one of the at least one shifted beamlet beingmelted throughout its entire thickness, each region of the at least aportion of the metal layer overlapped by a respective one of the atleast one shifted shadow region remaining at least partially unmelted,each at least partially unmelted region adjoining at least one meltedregion, wherein the intensity pattern of the further radiation beampulse is shifted with respect to the at least a portion of the metallayer by shifting the mask; (d) permitting each melted region of the atleast a portion of the metal layer irradiated by the further radiationbeam pulse to resolidify, wherein during resolidification of each meltedregion, grains grow therein from each one of the at least one adjoiningat least partially unmelted region, the further radiation beam pulsebeing the previous radiation beam pulse for further processing; and (e)repeating steps (c) and (d) in combination, if needed, with the furtherradiation beam pulse in each step becoming the previous radiation beampulse in the next step, until a desired grain structure is obtained inthe at least a portion of the metal layer.
 3. A method for processing athin metal layer disposed on a substrate comprising the steps of: (a)irradiating at least a portion of the metal layer with a first radiationbeam pulse having an intensity pattern that includes at least onebeamlet and at least one shadow region, each region of the at least aportion of the metal layer overlapped by a respective one of the atleast one beamlet being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one shadow region remaining at leastpartially unmelted, each at least partially unmelted region adjoining atleast one adjacent melted region, wherein the metal layer comprises atleast one metal layer strip each having a predefined contour and theintensity pattern of the first radiation beam pulse has at least onestring of multiple, relatively small, regularly spaced-apart, dot-likeshadow regions, each string of shadow regions conforming to a respectivepredefined contour and overlapping a respective one of the at least onemetal layer strip having the same predefined contour; (b) permittingeach melted region of the at least a portion of the metal layerirradiated by the first radiation beam pulse to resolidify, whereinduring resolidification of each melted region, grains grow therein fromeach one of the at least one adjoining at least partially unmeltedregion, (c) irradiating at least a portion of the metal layer with afurther radiation beam pulse having the same intensity pattern as theprevious radiation beam pulse, wherein the previous radiation beam pulseis the first radiation beam pulse of step (a), but where the at leastone beamlet and the at least one shadow region thereof are shifted withrespect to the at least a portion of the metal layer, each region of theat least a portion of the metal layer overlapped by a respective one ofthe at least one shifted beamlet being melted throughout its entirethickness, each region of the at least a portion of the metal layeroverlapped by a respective one of the at least one shifted shadow regionremaining at least partially unmelted, each at least partially unmeltedregion adjoining at least one melted region; (d) permitting each meltedregion of the at least a portion of the metal layer irradiated by thefurther radiation beam pulse to resolidify, wherein duringresolidification of each melted region, grains grow therein from eachone of the at least one adjoining at least partially unmelted region,the further radiation beam pulse being the previous radiation beam pulsefor further processing; and (e) repeating steps (c) and (d) incombination, if needed, with the further radiation beam pulse in eachstep becoming the previous radiation beam pulse in the next step, untila desired grain structure is obtained in the at least a portion of themetal layer.
 4. The method of claim 3, wherein the desired grainstructure of each one of the at least one metal layer strip comprises aplurality of single grain regions separated by respective grainboundaries, each grain boundary being approximately perpendicular to themetal layer strip at the location of the grain boundary.
 5. A method forprocessing a thin metal layer disposed on a substrate comprising thesteps of: (a) irradiating at least a portion of the metal layer with afirst radiation beam pulse having an intensity pattern that includes atleast one beamlet and at least one shadow region, each region of the atleast a portion of the metal layer overlapped by a respective one of theat least one beamlet being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one shadow region remaining at leastpartially unmelted, each at least partially unmelted region adjoining atleast one adjacent melted region, wherein the metal layer comprises atleast one metal layer strip each having a respective predefined contour,and the intensity pattern of the first radiation beam pulse has at leastone relatively narrow, strip-like shadow region, each one of the atleast one strip-like shadow region having a respective one of thepredefined contour of each one of the at least one metal layer strip,and overlapping a respective one of the at least one metal layer striphaving the same predefined contour; (b) permitting each melted region ofthe at least a portion of the metal layer irradiated by the firstradiation beam pulse to resolidify, wherein during resolidification ofeach melted region, grains grow therein from each one of the at leastone adjoining at least partially unmelted region; (c) irradiating atleast a portion of the metal layer with a further radiation beam pulsehaving the same intensity pattern as the previous radiation beam pulse,wherein the previous radiation beam pulse is the first radiation beampulse of step (a), but where the at least one beamlet and the at leastone shadow region thereof are shifted with respect to the at least aportion of the metal layer, each region of the at least a portion of themetal layer overlapped by a respective one of the at least one shiftedbeamlet being melted throughout its entire thickness, each region of theat least a portion of the metal layer overlapped by a respective one ofthe at least one shifted shadow region remaining at least partiallyunmelted, each at least partially unmelted region adjoining at least onemelted region; (d) permitting each melted region of the at least aportion of the metal layer irradiated by the further radiation beampulse to resolidify, wherein during resolidification of each meltedregion, grains grow therein from each one of the at least one adjoiningat least partially unmelted region, the further radiation beam pulsebeing the previous radiation beam pulse for further processing; and (e)repeating steps (c) and (d) in combination, if needed, with the furtherradiation beam pulse in each step becoming the previous radiation beampulse in the next step, until a desired grain structure is obtained inthe at least a portion of the metal layer.
 6. A method for processing athin metal layer disposed on a substrate comprising the steps of: (a)irradiating at least a portion of the metal layer with a first radiationbeam pulse having an intensity pattern that includes at least onebeamlet and at least one shadow region, each region of the at least aportion of the metal layer overlapped by a respective one of the atleast one beamlet being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one shadow region remaining at leastpartially unmelted, each at least partially unmelted region adjoining atleast one adjacent melted region, wherein the intensity pattern of eachradiation beam pulse includes a multiplicity of relatively small,dot-like shadow regions disposed in a regular array, the spacingsbetween adjacent shadow regions being such that grains growing from eachat least partially unmelted region of the at least a portion of themetal layer abut grains growing from adjacent at least partiallyunmelted regions; (b) permitting each melted region of the at least aportion of the metal layer irradiated by the first radiation beam pulseto resolidify, wherein during resolidification of each melted region,grains grow therein from each one of the at least one adjoining at leastpartially unmelted region; (c) irradiating at least a portion of themetal layer with a further radiation beam pulse having the sameintensity pattern as the previous radiation beam pulse, wherein theprevious radiation beam pulse is the first radiation beam pulse of step(a), but where the at least one beamlet and the at least one shadowregion thereof are shifted with respect to the at least a portion of themetal layer, each region of the at least a portion of the metal layeroverlapped by a respective one of the at least one shifted beamlet beingmelted throughout its entire thickness, each region of the at least aportion of the metal layer overlapped by a respective one of the atleast one shifted shadow region remaining at least partially unmelted,each at least partially unmelted region adjoining at least one meltedregion; (d) permitting each melted region of the at least a portion ofthe metal layer irradiated by the further radiation beam pulse toresolidify, wherein during resolidification of each melted region,grains grow therein from each one of the at least one adjoining at leastpartially unmelted region, the further radiation beam pulse being theprevious radiation beam pulse for further processing; and (e) repeatingsteps (c) and (d) in combination, if needed, with the further radiationbeam pulse in each step becoming the previous radiation beam pulse inthe next step, until a desired grain structure is obtained in the atleast a portion of the metal layer.
 7. The method of claim 6, whereinthe multiplicity of relatively small, dot-like shadow regions aredisposed at respective intersections of regular spaced-apart,mutually-perpendicular diagonal lines, and wherein the desired grainstructure comprises approximately square-shaped single grain regions. 8.A method for processing a thin metal layer disposed on a substratecomprising the steps of: (a) irradiating at least a portion of the metallayer with a first radiation beam pulse having an intensity pattern thatincludes at least one beamlet and at least one shadow region, eachregion of the at least a portion of the metal layer overlapped by arespective one of the at least one beamlet being melted throughout itsentire thickness, each region of the at least a portion of the metallayer overlapped by a respective one of the at least one shadow regionremaining at least partially unmelted, each at least partially unmeltedregion adjoining at least one adjacent melted region, wherein theintensity pattern of each radiation beam pulse comprises a plurality ofregularly spaced-apart, elongated shadow regions and a plurality ofregularly spaced-apart, elongated beamlets, each beamlet beingpositioned in between and adjoining respective adjacent shadow regions,each region of the at least a portion of the metal layer overlapped by arespective one of the beamlets being melted throughout its entirethickness, each region of the at least a portion of the metal layeroverlapped by a respective one of the shadow regions remaining at leastpartially unmelted, each one of the at least partially unmelted regionsadjoining respective adjacent melted regions; (b) permitting each meltedregion of the at least a portion of the metal layer irradiated by thefirst radiation beam pulse to resolidify, wherein duringresolidification of each melted region, grains grow therein from eachone of the at least one adjoining at least partially unmelted region;(c) irradiating at least a portion of the metal layer with a furtherradiation beam pulse having the same intensity pattern as the previousradiation beam pulse, wherein the previous radiation beam pulse is thefirst radiation beam pulse of step (a), but where the at least onebeamlet and the at least one shadow region thereof are shifted withrespect to the at least a portion of the metal layer in a directionperpendicular to the elongated shadow regions and beamlets of theintensity pattern of the previous radiation beam pulse, each region ofthe at least a portion of the metal layer overlapped by a respective oneof the at least one shifted beamlet being melted throughout its entirethickness, each region of the at least a portion of the metal layeroverlapped by a respective one of the at least one shifted shadow regionremaining at least partially unmelted, each at least partially unmeltedregion adjoining at least one melted region; (d) permitting each meltedregion of the at least a portion of the metal layer irradiated by thefurther radiation beam pulse to resolidify, wherein duringresolidification of each melted region, grains grow therein from eachone of the at least one adjoining at least partially unmelted region,the further radiation beam pulse being the previous radiation beam pulsefor further processing; and (e) repeating steps (c) and (d) incombination, if needed, with the further radiation beam pulse in eachstep becoming the previous radiation beam pulse in the next step, untila desired grain structure is obtained in the at least a portion of themetal layer.
 9. The method of claim 8, wherein the beamlets are each inthe shape of repeating chevrons, and adjacent repeating chevron-shapedbeamlets are staggered with respect to one another such that upwardpointing apexes of each one of the repeating chevron-shaped beamlets arealigned with respective downward pointing apexes of adjacent repeatingchevron-shaped beamlets, and downward pointing apexes of each one of therepeating chevron-shaped beamlets are aligned with respective upwardpointing apexes of adjacent repeating chevron-shaped beamlets, andwherein the desired grain structure comprises adjoining single grainregions having a generally hexagonal shape.
 10. A method for processinga thin metal layer disposed on a substrate comprising the steps of: (a)irradiating at least a portion of the metal layer with a first radiationbeam pulse having an intensity pattern that includes a plurality ofregularly spaced-apart, relatively narrow, linear, stripe-like shadowregions, and a plurality of regularly spaced-apart, relatively wide,linear, stripe-like beamlets, each one of the beamlets being positionedin between and adjoining respective adjacent shadow regions, each regionof the at least a portion of the metal layer overlapped by a respectiveone of the beamlets being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the shadow regions remaining at least partiallyunmelted, each one of the at least partially unmelted regions adjoiningrespective adjacent melted regions; (b) permitting each melted region ofthe at least a portion of the metal layer to resolidify afterirradiation by the first radiation beam pulse, wherein duringresolidification of each melted region, grains grow therein fromadjoining at least partially unmelted regions in opposite directionstowards one another, and abut one another along a respective one of aplurality of first grain abutment boundaries; (c) irradiating the atleast a portion of the metal layer with a second radiation beam pulsehaving the same intensity pattern as the first radiation beam pulse, butwhere the shadow regions and beamlets thereof are shifted with respectto the at least a portion of the metal layer in a directionperpendicular to the beamlets and shadow regions by a distance at leastequal to the width of the shadow regions of the intensity pattern, eachregion of the at least a portion of the metal layer overlapped by arespective one of the shifted beamlets being melted throughout itsentire thickness, each region of the at least a portion of the metallayer overlapped by a respective one of the shifted shadow regionsremaining at least partially unmelted, each one of the at leastpartially unmelted regions adjoining respective adjacent melted regions;and (d) permitting each melted region of the at least a portion of themetal layer to resolidify after irradiation by the second radiation beampulse, wherein during resolidification of each melted region, respectivesingle grains grow therein from adjoining at least partially unmeltedregions in opposite directions towards one another, and abut one anotheralong a respective one of a plurality second grain abutment boundaries,and wherein upon completion of resolidification of each melted regionafter irradiation by the second radiation beam pulse, the at least aportion of the metal layer has a grain structure comprising relativelylong single grains extending between respective adjacent second grainabutment boundaries and having lateral grain boundaries approximatelyperpendicular to the second grain abutment boundaries.
 11. The method ofclaim 10, wherein each of the first and second radiation beam pulses isa laser beam pulse.
 12. The method of claim 11, wherein each of thefirst and second radiation beam pulses is an excimer laser beam pulse.13. The method of claim 11, wherein the respective intensity pattern ofthe first and second radiation beam pulses are each defined by a maskthrough which the first and second radiation beam pulses pass, and theshadow regions and beamlets of the intensity pattern of the secondradiation beam pulse are shifted with respect to the at least a portionof the metal layer by shifting the substrate having the metal layer. 14.The method of claim 13, wherein the mask is a projection mask.
 15. Themethod of claim 13, wherein the mask is a proximity mask.
 16. The methodof claim 13, wherein the mask is a contact mask.
 17. The method of claim11, wherein the respective intensity patterns of the first and secondradiation beam pulses are defined by a mask through which the first andsecond radiation beam pulses pass, and the shadow regions and beamletsof the intensity patterns of the first second radiation beam pulse areshifted with respect to the at least a portion of the metal layer byshifting the mask.
 18. The method of claim 10, wherein each one of thefirst and second radiation beam pulses is a electron beam pulse.
 19. Themethod of claim 10, wherein each one of the first and second radiationbeam pulses is an ion beam pulse.
 20. The method of claim 10, furthercomprising the steps of: (e) after resolidification of the meltedregions of the least a portion of the metal layer following irradiationby the second radiation beam pulse, rotating the metal layer on thesubstrate by 90° with respect to the second grain abutment boundaries;(f) irradiating the at least a portion of the metal layer with a thirdradiation beam pulse having an intensity pattern that includes aplurality of regularly spaced-apart, relatively-narrow, linear,stripe-like shadow regions and a plurality of regularly spaced-apart,relatively wide, linear, stripe-like beamlets, each one of the beamletsbeing positioned in between and adjoining respective adjacent shadowregions, each one of the shadow regions and beamlets being approximatelyperpendicular to the second grain abutment boundaries, each region ofthe at least a portion of the metal layer overlapped by a respective oneof the beamlets being melted throughout its entire thickness, eachregion of the at least a portion of the metal layer overlapped by arespective one of the shadow regions remaining at least partiallyunmelted, each one of the at least partially unmelted regions adjoiningrespective adjacent melted regions; (g) permitting each melted region ofthe at least a portion of the metal layer to resolidify afterirradiation by the third radiation beam pulse, wherein duringresolidification of each melted region, different single grains growfrom each at least partially unmelted region into each adjoining meltedregion, and in each melted region respective single grains grow fromadjoining at least partially unmelted regions in opposite directionstowards one another, and abut one another along a respective one of aplurality of third grain abutment boundaries, each one of the abuttingsingle grains having a dimension in a direction parallel to the thirdgrain abutment boundaries approximately equal to the distance betweenadjacent second grain abutment boundaries; (h) irradiating the at leasta portion of the metal layer with a fourth radiation beam pulse havingthe same intensity pattern as the third radiation beam pulse, but wherethe shadow regions and beamlets thereof are each shifted with respect tothe at least a portion of the metal layer in a direction approximatelyperpendicular to the third grain abutment boundaries by a distance atleast equal to the width of the shadow regions of the intensity pattern,each region of the at least a portion of the metal layer overlapped by arespective one of the shifted beamlets being melted throughout itsentire thickness, each region of the at least a portion of the metallayer overlapped by a respective one of the shifted shadow regionsremaining at least partially unmelted, each one of the at leastpartially unmelted regions adjoining respective adjacent melted regions;and (i) permitting each melted region of the at least a portion of themetal layer to resolidify after irradiation by the fourth radiation beampulse, wherein during resolidification of each melted region, respectivesingle grains grow from each at least partially unmelted region intoeach adjoining melted region, and in each one of the melted regions,respective single grains grow from adjoining at least partially unmeltedregions in opposite directions towards one another, and abut one anotherat a respective one of a plurality of fourth grain abutment boundaries,and wherein upon completion of resolidification of the melted regions,the at least a portion of the metal layer has a grain structurecomprising an array of generally rectangular-shaped single grain regionsin respective rows and columns, each generally rectangular-shaped singlegrain region having a dimension on two opposing sides substantiallyequal to the distance between adjacent second grain abutment boundariesand having a dimension on the other two opposing sides substantiallyequal to the distance between adjacent fourth grain abutment boundaries.21. The method of claim 10, wherein the metal layer is formed of one ofan elemental metal, a compound metal and an alloy metal.
 22. The methodof claim 10, wherein the metal layer is formed of one of aluminum,copper, tungsten, titanium, platinum and gold.
 23. The method of claim10, wherein the metal layer is disposed on a substrate having adiffusion barrier layer.
 24. The method of claim 10, wherein the metallayer is formed on the substrate having a diffusion barrier layer formedof one of silicon dioxide, tantalum and a tantalum compound.
 25. Themethod of claim 10, wherein the at least a portion of the metal layer issubdivided into a plurality of sections, and steps (a), (b), (c) and (d)are carried out in combination in each one of the sections, one sectionat a time.
 26. The method of claim 25, wherein the at least a portion ofthe metal layer is subdivided into contiguous sections, and steps (a),(b), (c) and (d) are carried out in combination in successive contiguousones of the sections one section at a time, and wherein the irradiationof steps (a) and (b) each overlap a previous contiguous section by arelatively small area.
 27. The method of claim 10, wherein the at leasta portion of the metal layer is subdivided into a plurality of sections,and steps (a), (b), (c) and (d) are separately carried out one step at atime in each one of the sections, one section at a time.
 28. The methodof claim 27, wherein the at least a portion of the metal layer issubdivided into contiguous sections, and steps (a), (b), (c) and (d) areseparately carried out one step at a time in successive contiguous onesof the sections, one section at a time, and wherein the irradiation ofsteps (a) and (c) each overlap a previous contiguous section by arelatively small area.
 29. A method for processing a thin metal layerdisposed on a substrate, the metal layer comprising at least onerelatively narrow metal layer strip each having a respective one of atleast one predefined contour conforming to a Manhattan geometry, themethod comprising the steps of: (j) irradiating the at least one metallayer strip with a first radiation beam pulse having an intensitypattern that includes a plurality of relatively narrow, linear,stripe-like shadow regions overlapping each one of the at least onemetal layer strip at regular intervals along its respective predefinedcontour and a beamlet overlapping all regions of the at least one metallayer strip not overlapped by one of the shadow regions, each region ofthe at least one metal layer strip overlapped by the beamlet beingmelted throughout its entire thickness, each region of the at least onemetal layer strip overlapped by a respective one of the shadow regionsremaining at least partially unmelted, each one of the at leastpartially unmelted regions adjoining respective adjacent melted regions;(k) permitting each melted region of the at least one metal layer stripto resolidify after being irradiated by the first radiation beam pulse,wherein during resolidification of each melted region, different singlegrains grow from each one of the at least partially unmelted regionsinto each adjoining melted region, and in each melted region respectivesingle grains grow from adjoining at least partially unmelted regions inopposite directions towards one another, and abut one another at arespective one of a plurality of first grain abutment boundaries; (l)irradiating the at least one metal layer with a second radiation beampulse having the same intensity pattern as the first radiation beampulse, but where the shadow regions and the beamlet thereof are shiftedsuch that the shadow regions are shifted along each one of the at leastone metal layer strip by a distance greater than the width of the shadowregions of the intensity pattern but less than the distance that wouldcause the shifted shadow regions to overlap the first grain abutmentboundaries, each region of the at least one metal layer strip overlappedby the shifted beamlet being melted throughout its entire thickness,each region of the at least one metal layer strip overlapped by arespective one of the shifted shadow regions remaining at leastpartially unmelted, each one of the at least partially unmelted regionsadjoining respective adjacent melted regions; and (m) permitting eachmelted region of the at least one metal layer strip to resolidify afterbeing irradiated by the second radiation beam pulse, wherein duringresolidification of each melted region, a respective single grain growsfrom each at least partially unmelted region into each adjoining meltedregions, and in each melted region respective single grains grow fromadjoining at least partially unmelted regions in opposite directionstowards one another, and abut one another at a respective one of aplurality of second grain abutment boundaries, and wherein aftercompletion of resolidification following irradiation by the secondradiation beam pulse, each one of the at least one metal layer strip hasa grain structure comprising single grain regions extending betweenrespective adjacent second grain abutment boundaries, each second grainabutment boundary being approximately perpendicular to a respective oneof the at least one metal layer strip at the location of the secondgrain abutment boundary.
 30. The method of claim 29, wherein each of thefirst and second radiation beam pulses is a laser beam pulse.
 31. Themethod of claim 29, wherein each of the first and second radiation beampulses is an excimer laser beam pulse.
 32. The method of claim 29,wherein each of the first and second radiation beam pulses is a electronbeam pulse.
 33. The method of claim 29, wherein each of the first andsecond radiation beam pulses is a ion beam pulse.
 34. The method ofclaim 29, wherein each of the first and second radiation beam pulses isa laser pulse, and the intensity patterns of the first and secondradiation beam pulses are defined by a mask through which the first andsecond radiation beam pulses pass, the intensity pattern of the secondradiation beam pulse being shifted with respect to the at least onemetal layer strip by shifting the substrate having the at least onemetal layer strip.
 35. The method of claim 29, wherein each of the firstand second radiation beam pulses is a laser beam pulse, and therespective intensity patterns of the first and second radiation beampulses are defined by a mask through which the first and secondradiation beam pulses pass, the intensity pattern of the secondradiation beam pulse being shifted with respect to the at least onemetal layer strip by shifting the mask.
 36. A method for processing athin metal layer, the metal layer comprising at least one relativelynarrow metal layer strip having at least one segment and a respectivepredefined contour conforming to a Manhattan geometry, the methodcomprising the steps of: (n) irradiating the at least one metal layerstrip with a first radiation beam pulse having an intensity pattern thatincludes a plurality of regularly spaced-apart, relatively narrow,linear, stripe-like shadow regions and a plurality of regularlyspaced-apart, relatively wide, linear, stripe-like beamlets, each one ofthe beamlets being positioned in between and adjoining respectiveadjacent shadow regions, each segment of the at least one metal layerstrip being diagonally oriented with respect to the shadow regions andthe beamlets, each region of the at least one metal layer stripoverlapped by a respective one of the beamlets being melted throughoutits entire thickness, each region of the at least one metal layer stripoverlapped by a respective one of the shadow regions remaining at leastpartially unmelted, each one of the at least partially unmelted regionsadjoining respective adjacent melted regions; (o) permitting each meltedregion of the at least one metal layer strip to resolidify afterirradiation by the first radiation beam pulse, wherein duringresolidification of each melted region, different single grains growfrom each at least partially unmelted region into each adjoining meltedregion, and in each melted region respective single grains grow fromadjoining at least partially unmelted regions in opposite directionstowards one another, and abut one another at a respective one of aplurality of first grain abutment boundaries, each one of the firstgrain abutment boundaries being approximately perpendicular to arespective one of the at least one metal layer strip at the location ofthe first grain abutment boundary; (p) irradiating the at least onemetal layer strip by a second radiation beam pulse having the sameintensity pattern as the first radiation beam pulse, but where theshadow regions and beamlets thereof are shifted with respect to the atleast one metal layer strip in a direction perpendicular to the shadowregions and beamlets of the intensity pattern of the first radiationbeam pulse by a distance greater than the width of the shadow regions ofthe intensity pattern but less than the distance that would cause theshifted shadow regions to overlap the first grain abutment boundaries,each region of the at least one metal layer strip overlapped by arespective one of the shifted beamlets being melted throughout itsentire thickness, each region of the at least one metal layer stripoverlapped by a respective one of the shifted shadow regions remainingat least partially unmelted, each one of the at least partially unmeltedregions adjoining respective adjacent melted regions; and d) permittingeach melted region of the at least one metal layer strip to resolidifyafter irradiation by the second radiation beam pulse, wherein duringresolidification of each melted region, a respective single grain growsfrom each at least partially unmelted region into each adjoining meltedregion, and in each melted region respective single grains grow fromadjoining at least partially unmelted regions in opposite directionstowards one another, and abut one another at a respective one of aplurality of second grain abutment boundaries, each second grainabutment boundary being approximately perpendicular to a respective oneof the at least one metal layer strip at the location of the secondgrain abutment boundary, and wherein after completion ofresolidification following irradiation by the second radiation beampulse each one of the at least one metal layer strip has a grainstructure comprising single grain regions extending between respectiveadjacent second grain abutment boundaries.
 37. A method for processing athin metal layer disposed on a substrate comprising the steps of: (q)irradiating at least a portion of the metal layer by a radiation beampulse having an intensity pattern that includes a stripe-shaped beamlethaving a predefined contour and a shadow region that overlaps allregions of the at least a portion of the metal layer not overlapped bythe beamlet, a region of the at least a portion of the metal layeroverlapped by the beamlet being melted throughout its entire thicknessso as to form a melted region having the predefined contour, each regionof the at least a portion of the metal layer overlapped by the shadowregion remaining at least partially unmelted, the melted region beingsurrounded by an unmelted region that adjoins the melted region alongfirst and second opposing edges of the melted region; (r) permitting themelted region to resolidify after irradiation by the radiation beampulse to form a resolidification region having the predefined contour,wherein during resolidification of the melted region to form theresolidification region, first and second rows of grains grow from thefirst and second opposing edges of the melted region, respectively, inopposite directions towards one another; and (s) after the melted regionhas completely resolidified, patterning the metal layer to form at leastone relatively narrow metal layer strip formed from a strip-shapedregion having the predefined contour in one of the first and second rowsof grains in the resolidification region, the metal layer strip havingthe predefined contour and single grain regions separated by respectivegrain boundaries, each grain boundary forming a relatively large anglewith respect to the metal layer strip at the location of the grainboundary.
 38. The method of claim 37, wherein during resolidification ofthe melted region, the first and second rows of grains grow in oppositedirections towards one another until the first and second rows of grainsabut one another along a grain abutment boundary that extends centrallythrough the resolidified region and that has the predefined contour. 39.The method of claim 37, wherein the radiation beam pulse is a laser beampulse.
 40. The method of claim 39, wherein the laser beam pulse is anexcimer laser beam pulse.
 41. The method of claim 37, wherein theradiation beam pulse is a electron beam pulse.
 42. The method of claim37, wherein the radiation beam pulse is an ion beam pulse.
 43. Themethod of claim 37, wherein the intensity pattern of the radiation beampulse is defined by a mask through which the radiation beam pulsepasses.
 44. The method of claim 43, wherein the mask is a projectionmask.
 45. The method of claim 43, wherein the mask is a proximity mask.46. The method of claim 43, wherein the mask is a contact mask.
 47. Amethod for processing a thin metal layer disposed on the substratecomprising the steps of: (t) dividing for processing purposes at least aportion of the metal layer into a plurality of columns having apredetermined width; (u) irradiating a first column in a first pass witha pulsed radiation beam having a predetermined pulsed repetition rate bytranslating the substrate having the metal layer at a predeterminedtranslation velocity past a position of impingement of the pulsedradiation beam so that the pulsed radiation beam scans the entire lengthof the first column along a first irradiation path, each pulse of thepulsed radiation beam having an intensity pattern that includes aplurality of shadow regions and a plurality of beamlets, the intensitypattern of each pulse of the pulsed radiation beam having a width atleast equal to the predetermined width of the columns, wherein duringeach pulse of the pulsed radiation beam, each region of the at least aportion of the metal layer overlapped by a respective one of thebeamlets is melted throughout its entire thickness, and each region ofthe at least a portion of the metal layer overlapped by a respective oneof the shadow regions remains at least partially unmelted, each at leastpartially unmelted region adjoining respective adjacent melted regions,the predetermined translation velocity of the metal layer and thepredetermined pulse repetition rate of the pulsed radiation beam beingchosen so that a melted region in a previous portion of the at least aportion of the metal layer irradiated by a previous pulse of the pulsedradiation beam completely resolidifies before a next portion whichpartially overlaps the previous portion is irradiated by a next pulse ofthe pulsed radiation beam, the first pass being a previous pass and thefirst irradiation path being a previous irradiation path for furtherprocessing; (v) shifting the substrate having the metal layer by arelatively small distance in a direction perpendicular to the columns tothereby shift the shadow regions and beamlets of the intensity patternof each pulse of the pulsed radiation beam with respect to the at leasta portion of the metal layer; (w) irradiating the first column in a nextpass with the pulsed radiation beam having the predetermined pulserepetition rate and the shifted radiation beam pulse intensity patternby translating the substrate having the metal layer at the predeterminedtranslation velocity past the position of impingement of the pulsedradiation beam so that the pulsed radiation beam scans the entire lengthof the first column in a next pass along a next irradiation path,wherein during each pulse of the pulsed radiation beam, each region ofthe at least a portion of the metal layer overlapped by a respective oneof the shifted beamlets is melted throughout its entire thickness, andeach region of the at least a portion of the metal layer overlapped by arespective one of the shifted shadow regions remains at least partiallyunmelted, each one of the at least partially unmelted regions adjoiningrespective adjacent melted regions, the predetermined translationvelocity of the metal layer and the predetermined pulse repetition rateof the pulsed radiation beam being chosen so that a melted region in aprevious portion of the at least a portion of the metal layer irradiatedby a previous pulse of the pulsed radiation beam completely resolidifiesbefore a next portion which partially overlaps the previous portion isirradiated by a next pulse of the pulsed radiation beam; (x) repeatingsteps (c) and (d) in combination, if needed, with the next pass being aprevious pass and the next irradiation path being a previous irradiationpath for further processing until a desired grain structure is obtainedin the first column; (y) translating the substrate having the metallayer so that the metal layer is positioned with respect to the pulsedradiation beam for irradiation of a next column of the at least aportion of the metal layer in a first pass; (z) repeating steps (b), (c)and (d), and (e), if needed, in combination with the first column beingthe next column for further processing until a desired grain structureis obtained in the next column; and (aa) repeating steps (f) and (g) incombination with the next column being a further column for furtherprocessing until a desired grain structure is obtained in each column ofthe at least a portion of the metal layer.
 48. The method of claim 47,wherein the intensity pattern of each pulse of the pulsed radiation beamhas a plurality of regularly spaced-apart, relatively narrow, linear,stripe-like shadow regions and a plurality of regularly spaced-apart,relatively wide, linear, stripe-like beamlets, each one of the beamletsbeing positioned in between and adjoining respective adjacent shadowregions, the shadow regions and beamlets being parallel to the columnsof the at least a portion of the metal layer, and the shifting of themetal layer is by a distance that causes each one of the beamlets tooverlap a respective one of the at least partially unmelted regions inthe first pass and to partially overlap columns of grains in respectiveadjoining regions melted and resolidified in the first pass.
 49. Themethod of claim 47, wherein the pulsed radiation beam is a pulsed laserbeam.
 50. The method of claim 49, wherein the pulsed laser beam is apulsed excimer laser beam.
 51. The method of claim 47, wherein thepulsed radiation beam is a chopped continuous wave laser beam.
 52. Themethod of claim 47, wherein the pulsed radiation beam is a pulsedelectron beam.
 53. The method of claim 47, wherein the pulsed radiationbeam is a pulsed ion beam.